High transmission light control film

ABSTRACT

A light control film is described comprising alternating transmissive regions and absorptive regions disposed between a light input surface and a light output surface. The absorptive regions have an aspect ratio of at least 30. In some embodiments, the alternating transmissive regions and absorptive regions have a transmission as measured with a spectrophotometer at a viewing angle of 0 degrees of at least 35, 40, 45, or 50% for a wavelength of the range 320-400 nm (UV) and/or at least 65, 70, 75, or 80% for a wavelength of the range 700-1400 nm (NIR). In another embodiment, the absorptive regions block light at the light input surface and light output surface and the maximum surface area that is blocked is less than 20% of the total alternating transmissive regions and absorptive regions. Also described are various optical communication systems comprising the light control films described herein and methods.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1a is a cross-sectional view of an embodied light control film.

FIG. 1b depicts the polar cut-off viewing angle of the light control film of FIG. 1 a.

FIG. 1c is a perspective view of a comparative microstructured film.

FIG. 2 is a perspective view of a microstructured film.

FIG. 3 is a cross-sectional schematic of an embodied method of making a light control film.

FIG. 4 is a perspective view of a light control film further comprising a cover film bonded with an adhesive layer.

FIG. 5 is a perspective schematic of a backlit display comprising an embodied light control film.

FIG. 6 is a plot of luminance versus viewing angle for various light control films.

FIG. 7 is a schematic cross-sectional view of an exemplary light control film applied to a window of an enclosure, such as a building, a house or a vehicle.

FIG. 8 is a schematic plot of transmission of a light control film vs. wavelength.

FIG. 9 is a schematic view of an exemplary application where a light control film is applied to a plane or an aircraft.

FIG. 10 is a schematic cross-sectional view of an exemplary optical communication system including a light control film combined with a retroreflector, and

FIG. 11 is a schematic cross-sectional view of an exemplary wearable optical communication system including a light control film and a wrist watch with a pulse sensor.

SUMMARY

Although various light control films have been described, industry would find advantage in light control films suitable for use as a privacy film having improved properties such as improved on-axis transmission.

In one embodiment, a light control film is described comprising a light input surface and a light output surface opposite the light input surface and alternating transmissive regions and absorptive regions disposed between the light input surface and the light output surface.

In one embodiment, the absorptive regions have an aspect ratio of at least 30.

In some embodiments, the alternating transmissive regions and absorptive regions have a relative transmission (as measured with a conoscope) at a viewing angle of 0 degrees of at least 75%.

In another embodiment, the alternating transmissive region and absorptive regions have a transmission as measured with a spectrophotometer at a viewing angle of 0 degrees of at least 35, 40, 45, or 50% for a wavelength of the range 320-400 nm (UV).

In another embodiment, the alternating transmissive region and absorptive regions have a transmission as measured with a spectrophotometer at a viewing angle of 0 degrees of at least 65, 70, 75, or 80% for a wavelength of the range 700-1400 nm (NIR), or a combination thereof.

In yet another embodiment, a light control film is described comprising a light input surface and a light output surface opposite the light input surface and alternating transmissive regions and absorptive regions disposed between the light input surface and the light output surface. The absorptive regions block light at the light input surface and light output surface and the maximum surface area that is blocked is less than 20% of the total alternating transmissive regions and absorptive regions.

In another embodiment, the absorptive regions comprise a plurality of particles having a median particle size of less than 100 nanometers.

In another embodiment, the absorptive regions comprise a polyelectrolyte.

In some embodiments, the light control film further comprises additional layers such as a topcoat or adhesive and cover film and the total light control film has specified transmission properties as described herein.

In another embodiment, the light control film comprises a first light control film as just described disposed upon a second light control film. The second light control film may also have absorptive regions that have an aspect ratio of at least 30.

Also described are various optical communication systems comprising the light control films described herein.

In yet another embodiment, a method of making a light control film is described comprising: providing a microstructured film comprising a plurality of light transmissive regions alternated with channels, wherein the microstructured film has a surface defined by a top surface and side walls of the light transmissive regions and a bottom surface of the channels; applying an organic light absorptive material to the surface, and

removing at least a portion of the light absorptive coating from the top surface of the light transmissive regions and bottom surface of the channels.

In yet another embodiment, a method of making a microstructured film is described comprising: providing a microstructured film comprising a plurality of light transmissive regions alternated with channels, wherein the microstructured film has a surface defined by a top surface and side walls of the light transmissive regions and a bottom surface of the channels; applying a light absorptive material to the surface by layer-by-layer self-assembly; removing at least a portion of the light absorptive coating from the top surface of the light transmissive regions and bottom surface of the channels.

DETAILED DESCRIPTION

In one embodiment, a light control film (“LCF”) is described. With reference to FIG. 1a , a cross-sectional view of an embodied LCF 100, the LCF comprises a light output surface 120 and an opposing light input surface 110. The light output surface 120 is typically parallel to the light input surface 110. LCF 100 includes alternating transmissive regions 130 and absorptive regions 140 disposed between the light output surface 120 and a light input surface 110.

In one embodiment, as depicted in FIG. 1a , the transmissive regions 130 are typically integral with a land region “L”, meaning that there is no interface between the land region and the base portion 131 of the transmissive regions 130. Alternatively, LCF may lack such land region L or an interface may be present between the land region, L, and transmissive regions 130. When present, the land region is disposed between the alternating transmissive regions 130 and absorptive regions 140 and light input surface 110.

Alternatively, in another embodiment, surface 120 may be the light input surface and surface 110 may be the light output surface. In this embodiment, the land region is disposed between the alternating transmissive regions 130 and absorptive regions 140 and light output surface.

The transmissive regions 130 can be defined by a width “W_(T)”. Excluding the land region “L”, the transmissive regions 130 typically have nominally the same height as the absorptive regions 140. In typical embodiments, the height of the absorptive regions, H_(A), is at least 30, 40, 50, 60, 70, 80, 90 or 100 microns. In some embodiments, the height is no greater than 200, 190, 180, 170, 160, or 150 microns. In some embodiments, the height is no greater than 140, 130, 120, 110, or 100 microns. The LCF typically comprises a plurality of transmissive regions having nominally the same height and width. In some embodiments, the transmissive regions have a height, “HT”, a maximum width at its widest portion, “W_(T)”, and an aspect ratio, HT/W_(T), of at least 1.75. In some embodiments, HT/W_(T) is at least 2.0, 2.5, 3.0, 3.5, 4.0, 4.5 or 5.0. In other embodiments, the aspect ratio of the transmissive regions is at least 6, 7, 8, 9, 10. In other embodiments, the aspect ratio of the transmissive regions is at least 15, 20, 25, 30, 35, 40, 45, or 50.

Absorptive regions 140 have a height “H_(A)” defined by the distance between the bottom surface 155 and top surface 145, such top and bottom surfaces typically being parallel to the light output surface 120 and a light input surface 110. The absorptive regions 140 have a maximum width “W_(A)” and are spaced apart along surface light output surface 120 by a pitch “P_(A)”. The absorptive regions also have a length “L_(A)” as depicted in perspective views of FIG. 5. The width is typically the smallest dimension. The height is typically greater than the width. The length is typically the greatest dimension. In some embodiments, the length can span the entire length of a piece of film or span the length of an entire roll of film.

The width of the absorptive regions, W_(A), at the base (i.e. adjacent to bottom surface 155) is typically nominally the same as the width of the absorptive regions adjacent the top surface 145. However, when the width of the absorptive regions at the base differs from the width adjacent the top surface, the width is defined by the maximum width. The maximum width of a plurality of absorptive regions can be averaged for an area of interest, such as an area in which the transmission (e.g. brightness) is measured. The LCF typically comprises a plurality of absorptive regions having nominally the same height and width. In typical embodiments, the absorptive regions generally have a width no greater than 10, 9, 8, 7, 6, 5, 4, 3, 2, or 1 micron. In some embodiments, the absorptive regions generally have a width no greater than 900, 800, 700, 600, or 500 nanometers. In some embodiments, the absorptive regions have a width of at least 50, 60, 70, 80, 90, or 100 nanometers.

An absorptive region can be defined by an aspect ratio, the height of the absorptive region divided by the maximum width of the absorptive region (H_(A)/W_(A)). In some embodiments, the aspect ratio of the absorptive regions is at least 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10. In favored embodiments, the height and width of the absorptive region(s) are selected such that the absorptive region(s) have an even higher aspect ratio. In some embodiments, the aspect ratio of the absorptive regions is at least 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95 or 100. In other embodiments, the aspect ratio of the absorptive regions is at least 200, 300, 400, or 500. The aspect ratio can range up to 10,000 or greater. In some embodiments, the aspect ratio is no greater than 9,000; 8,000; 7,000; 6,000, 5,000; 4,000, 3000; 2,000, or 1,000.

As shown in FIG. 1b , LCF 100 includes alternating transmissive regions 130 and absorptive regions 140, and an interface 150 between transmissive regions 130 and absorptive regions 140. Interface 150 forms a wall angle θ with line 160 that is perpendicular to light output surface 120.

Larger wall angles θ decrease transmission at normal incidence or in other words a viewing angle of 0 degrees. Smaller wall angles are preferred such that the transmission of light at normal incidence can be made as large as possible. In some embodiments, the wall angle θ is less than 10, 9, 8, 7, 6, or 5 degrees. In some embodiments, the wall angle is no greater than 2.5, 2.0. 1.5, 1.0, 0.5, or 0.1 degrees. In some embodiments, the wall angle is zero or approaching zero. When the wall angle is zero, the angle between the absorptive regions and light output surface 120 is 90 degrees. Depending on the wall angle, the transmissive regions can have a rectangular or trapezoidal cross-section.

The transmission (e.g. brightness of visible light) can be increased when incident light undergoes total internal reflection (TIR) from the interface between the absorptive and transmissive regions. Whether a light ray will undergo TIR or not, can be determined from the incidence angle with the interface, and the difference in refractive index of the materials of the transmissive and absorptive regions.

As shown in FIG. 1b , transmissive regions 130 between absorptive regions 140 have an interface angle θ_(I) defined by the geometry of alternating transmissive regions 130 and absorptive regions. As depicted in FIGS. 1a and 1b , the interface angle θ_(I) can be defined by the intersection of two lines. The first line extends from a first point, defined by the bottom surface and the side wall surface of a first absorptive region, and a second point defined by the top surface and side wall surface of the nearest second absorptive region. The second line extends from a first point, defined by the top surface and the side wall surface of the first absorptive region, and a second point, defined by the bottom surface and side wall surface of the second absorptive region.

The polar cut-off viewing angle θP is equal to the sum of a polar cut-off viewing half angle θ1 and a polar cut-off viewing half angle θ2 each of which are measured from the normal to light input surface 110. In typical embodiments, the polar cut-off viewing angle θP is symmetric, and polar cut-off viewing half angle θ1 is equal to polar viewing half angle θ2. Alternatively, the polar cut-off viewing angle θP can be asymmetric, and polar cut-off viewing half angle θ1 is not equal to polar cut-off viewing half angle θ2.

Luminance can be measured according to the test method described in the examples. The luminance can be measured on the alternating transmissive and absorptive regions, such as illustrated in FIG. 1a or the total light control film that may further comprise a cover film, such as illustrated in FIG. 4. Relative transmission (e.g. brightness of visible light) is defined as the percentage of luminance, at a specified viewing angle or range of viewing angles, between a reading with the light control film including the alternating transmissive and absorptive regions and optionally other layers and a reading without the light control film (i.e. the baseline). With reference to FIG. 6, the viewing angle can range from −90 degrees to +90 degrees. A viewing angle of 0 degrees is orthogonal to light input surface 110; whereas viewing angles of −90 degrees and +90 degrees are parallel to light input surface 110.

For example, with reference to FIG. 6, the on-axis baseline luminance is 2100 Cd/m². EX. 6 has an on-axis luminance of 1910 Cd/m². Thus, the relative transmission (e.g. brightness) is 1910 Cd/m²/2100 Cd/m² multiplied by 100, which equals 91.0%. Unless specified otherwise, the relative transmission refers to the relative transmission of visible light having a 400-700 nm wavelength range as measured by the conoscope test method described in further detail in the examples.

The alternating transmissive and absorptive regions or total LCF can exhibit increased relative transmission (e.g. brightness) at a viewing angle of 0 degrees. In some embodiments, the relative transmission (e.g. brightness) is at least 75, 80, 85, or 90%. The relative transmission (e.g. brightness) is typically less than 100%.

The alternating transmissive and absorptive regions or total LCF can exhibit high transmission of other wavelengths of light at a viewing angle of 0 degrees. The transmission of near infrared (NIR) light having a wavelength range of the range 700-1400 nm and ultraviolet (UV) light having a wavelength range of 320-400 nm refers to transmission as measured by the spectrophotometry method described in further detail in the examples.

In some embodiments, the alternating transmissive and absorptive regions or total LCF has a transmission for a wavelength of the range 700-1400 nm (NIR) at a viewing angle of 0 degrees of at least 50, 55, 60, 65, 70, 75, or 80%. In some embodiments, the alternating transmissive and absorptive regions or total LCF has a transmission for a wavelength of the range 320-400 nm (UV) at a viewing angle of 0 degrees of at least 50% or 60%. The transmission can be for a single wavelength of the wavelength range or the transmission can be an average transmission for the entire wavelength range.

Alternatively, the alternating transmissive and absorptive regions or total LCF can exhibit low transmission of other wavelengths of light at a viewing angle of 0 degrees. The (e.g. PET) base film and material of the light transmissive regions and land layer can have high transmission of visible and NIR light, yet lower transmission of UV light. Further, inclusion of a (e.g. color shifting) film can substantially reduce the transmission of both UV and NIR light, while exhibiting high transmission of visible light. In some embodiments, the alternating transmissive and absorptive regions or total LCF have a transmission for a wavelength of the range 700-1400 nm (NIR) at a viewing angle of 0 degrees of less than 50, 45, 40, or 30%. In some embodiments, the alternating transmissive and absorptive regions or total LCF have a transmission for a wavelength of the range 320-400 nm (UV) at a viewing angle of 0 degrees of less than 50, 45, 40, 35, 30, 25, 20, 15, 10 or 5%. The transmission can be for a single wavelength of the wavelength range or the transmission can be an average transmission for the entire wavelength range.

In typical embodiments, the LCF has significantly lower transmission at other viewing angles. For example, in some embodiments, the relative transmission (e.g. brightness of visible light) at a viewing angle of −30 degrees, +30 degrees, or an average of −30 degrees and +30 degrees is less than 50, 45, 40, 35, 30, or 25%. In other embodiments, the relative transmission (e.g. brightness) at a viewing angle of 30 degrees, +30 degrees, or the average of −30 degrees and +30 degrees is less than 25, 20, 15, 10 or 5%. In some embodiments, the relative transmission (e.g. brightness) at a viewing angle of +/−35, +/−40, +/−45, +/−50, +1-55, +/−60, +/−65, +/−70, +/−75, or +/−80 degrees is less than 25, 20, 15, 10 or 5%, or less than 5%. In some embodiments, the average relative transmission (e.g. brightness) for viewing angles ranging from +35 to +80 degrees, −35 to −80 degrees, or the average of these ranges is less than 10, 9, 8, 7, 6, 5, 4, 3, or 2%.

The alternating transmissive and absorptive regions or total LCF can exhibit significantly lower transmission of NIR or UV wavelengths of light at other viewing angles. For example, in some embodiments, the alternating transmissive and absorptive regions or total light control film has a transmission for a wavelength range of 700-1400 nm (NIR) at a viewing angle of 30 degrees of less than 50, 45, 40, 35, 30, 25, 20, 15, 10 or 5%. In some embodiments, the alternating transmissive and absorptive regions or total light control film has a transmission at a wavelength range of 320-400 nm (UV) at a viewing angle of 30 degrees of less than 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 4, 3, 2, or 1%. In some embodiments, the transmission of NIR or UV wavelengths of light at viewing angles of 60 degrees also fall within the previously stated range and is typically lower than the transmission at 30 degrees. In some embodiments, the alternating transmissive and absorptive regions or total light control film has an average transmission for a wavelength range of 700-1400 nm (NIR) at a viewing angle of 60 degrees of less than 5, 4, 3, 2, or 1%.

Thus, the light control films described herein can exhibit various combinations of high and low transmission properties at various viewing angles for various wavelengths of light (visible, UV, and NIR).

In one embodiment, the light control film exhibits high transmission of NIR at various viewing angles (e.g. 0, 30, and 60 degrees), yet lower transmission of visible and UV, as previously described. The light control film can exhibit a transmission for a wavelength of the range 700-1400 nm (NIR) of at least 60, 65, 70, 75, or 80% and a transmission for a wavelength of the range 700-1400 nm (NIR) at a viewing angle of 30 and/or 60 degrees of at least 10, 15, 20, 25, 30, 35, 40, 45, or 50%.

LCFs with significantly lower transmission at “off-axis” viewing angles are suitable for use as privacy films. Such films allow a viewer directly in front of a display (viewing angle of 0 degrees) to see the image yet blocks viewers at “off-axis” angles from seeing such image.

The absorptive regions can be characterized with respect to the maximum surface area of absorptive regions that blocks (e.g. absorbs) light at the light input surface or light output surface. The light input or output surface of a light control film can be viewed with an optical microscope (e.g. at 200× magnification). For smaller absorptive regions (e.g. W_(A) less than 1 micron, a higher resolution microscope, (e.g scanning electron microscope) can be used to measure the surface area. The maximum width of multiple absorptive regions (i.e., W_(A) in FIG. 1a ) and pitches (i.e., P_(A) in FIG. 1a ) can be measured by analyzing the optical microscope images with ImageJ software (such as available from the National Institute of Health at http://imagej.nih.gov/ij).

FIG. 1c is a perspective view of a comparative LCF 150 that comprises a light output surface 120 and an opposing light input surface 110. The light output surface 120 is typically parallel to the light input surface 110. LCF 700 includes alternating transmissive regions 130 and absorptive regions 140 disposed between the light output surface 120 and a light input surface 110. For comparative light control films (CE2), as illustrated in FIG. 1c , the average maximum width of (e.g. five) absorptive regions, W_(A) is 15 microns. The average pitch, P_(A), (distance between absorptive regions) is 65 microns. The ratio W_(A)/P_(A) equals 0.23, or 23%. In other words, the maximum surface area the absorptive regions occupy is 23% of the total alternating transmissive and absorptive regions of the light output surface 720.

The absorptive regions presently described block (e.g. absorbs) less light than the comparative light control film. In typical embodiments, the maximum surface area the absorptive regions occupy is less than 20, 19, 18, 17, 16, 15, 14, 13, 12, 11, 10, 9, 8, 7, 6, 5, 4, or 3% of the total alternating transmissive and absorptive regions. When the absorptive regions have a wall angle of zero or in other words the height is orthogonal to the light input and output surface as depicted in FIG. 1a , the maximum surface area the absorptive regions occupy can be calculated in the same manner as the comparative light control film as just described (i.e. ratio W_(A)/P_(A)). When the absorptive regions have a wall angle of greater than zero, the ratio of W_(A)/P_(A) does not account for all the light that is blocked as light passes through the film in a direction orthogonal to the light input and light output surfaces. In this embodiment, “d” can be calculated from the wall angle and line 160 that is perpendicular to light output surface 120. This total surface area of light that is blocked is equal to (d+W_(A))/(W_(T)+W_(A)). For example, when W_(T) is 30 microns, W_(A) is 0.5 microns, and the wall angle is 3 degrees, (d+W_(A))/(W_(T)+W_(A))=)(tan(3°+0.5)/(30+0.5) and the total surface area of light blocked is 17.1%.

The absorptive regions can be formed by coating the surface of a microstructured film. FIG. 2 shows an embodied microstructured film article 200 that can be coated to make an LCF. The depicted microstructured film includes a microstructured surface 210 comprising a plurality of channels 201 a-201 d on base layer 260. As shown in FIG. 2, a continuous land layer “L” can be present between the bottom of the channels 205 and the top surface 210 of base layer 260. Alternatively, the channels 201 can extend all the way through the microstructured film article 200. In this embodiment (not shown), the bottom surface 205 of the groove can be coincident with the top surface 210 of a base layer 260. In typical embodiments, the base layer 260 is a preformed film that comprises a different organic polymeric material than the transmissive regions 230 as will subsequently be described.

The height and width of protrusions (e.g. transmissive regions) 230 are defined by adjacent channels (e.g. 201 a and 201 b). The protrusions (e.g. transmissive regions) 230 can be defined by a top surface 220, a bottom surface, 231, and side walls 232 and 233 that join the top surface to the bottom surface. The side walls can be parallel to each other. More typically the side walls have a wall angle as previously described.

In some embodiments, the protrusions (e.g. transmissive regions) 230 have a pitch, “PT” of at least 10 microns. The pitch is the distance between the onset of a first protrusion (e.g. transmissive region) and the onset of a second protrusion (e.g. transmissive region) as depicted in FIG. 2. The pitch may be at least 15, 20, 25, 30, 35, 40, 45, or 50 microns. The pitch is generally no greater than 1 mm. The pitch is typically no greater than 900, 800, 700, 600, or 500 microns. In some embodiments, the pitch is typically no greater than 550, 500, 450, 400, 350, 300, 250 or 200 microns. In some embodiments, the pitch is no greater than 175, 150, 100 microns. In typical embodiments, the protrusions are evenly spaced, having a single pitch. Alternatively, the protrusions may be spaced such that the pitch between adjacent protrusions is not the same. In this later embodiment, at least some and typically the majority (at least 50, 60, 70, 80, 90% or greater of the total protrusions) have the pitch just described. The pitch of the absorptive regions P_(A) is within the same range as just described for the light transmissive regions.

The pitch and height of the protrusions (e.g. transmissive regions) can be important to facilitate coating of the protrusions (e.g. transmissive regions) with a light absorbing coating. When the protrusions are spaced too close together it can be difficult to uniformly coat the side walls. When the protrusions are spaced too far apart, the light absorbing coating may not be effective at providing its intended function, such as privacy at off-axis viewing angles.

The absorptive regions are formed by providing a light absorptive coating on the side walls of protrusions (e.g. transmissive regions) of a microstructured film. The thickness of the light absorptive coating is equivalent to the width of the absorptive regions, W_(A), as previously described. The absorptive regions can be formed by any method that provides a sufficiently thin, conformal, light absorptive coating on the side walls (e.g. 232, 233).

In one embodiment, the absorptive regions are formed by a combination of additive and subtractive methods.

With reference to FIG. 3, the light control film can be prepared by providing a microstructured film 300 (such as the microstructured film of FIG. 2) comprising a plurality of protrusions (e.g. transmissive regions) defined by a top surface (e.g. 320) and side walls (332, 333). The plurality of protrusions (e.g. transmissive regions) 330 are separated from each other by channels 301 a and 301 b. The side walls of the protrusions (e.g. transmissive regions) are coincident with the side walls of the channels. The channels further comprise a bottom surface 305 that is parallel to or coincident with top surface of base layer 360. The method further comprises applying a light absorptive coating 341 to the (e.g. entire) surface of the microstructured film, i.e. the top surface 320 and side walls 332, 333 of the protrusions (e.g. transmissive regions) and the bottom surface 305 of the channels that separate the protrusions (e.g. transmissive regions). The method further comprises removing the coating from the top surface 320 of the protrusions (e.g. transmissive regions) and bottom surface 305 of the channels. In some embodiments, the method further comprises filling the channels with an organic polymeric material 345 such as (e.g. the same) polymerizable resin as the protrusions (e.g. transmissive regions) and curing the polymerizable resin. When the channels are not filled with a cured polymerizable resin, the channels are typically filled with air.

A microstructure-bearing article (e.g. microstructured film article 200 shown in FIG. 2) can be prepared by any suitable method. In one embodiment, the microstructure-bearing article (e.g. microstructured film article 200 shown in FIG. 2) can be prepared by a cast and cure method, as described in U.S. Pat. No. 8,096,667, including the steps of (a) preparing a polymerizable composition; (b) depositing the polymerizable composition onto a master negative microstructured molding surface (e.g. tool) in an amount barely sufficient to fill the cavities of the master; (c) filling the cavities by moving a bead of the polymerizable composition between a (e.g. preformed film) base layer and the master, at least one of which is flexible; and (d) curing the composition. The deposition temperature can range from ambient temperature to about 180° F. (82° C.). The master can be metallic, such as nickel, chrome- or nickel-plated copper or brass, or can be a thermoplastic material that is stable under the polymerization conditions and has a surface energy that allows clean removal of the polymerized material from the master. When the base layer is a preformed film, one or more of the surfaces of the film can optionally be primed or otherwise be treated to promote adhesion with the organic material of the light transmissive regions. In one embodiment, the base layer comprises a thermoset acrylic polymer as a primer such as available from Dow Chemical, Midland, Mich. under the trade designation “Rhoplex 3208”.

The polymerizable resin can comprise a combination of a first and second polymerizable component selected from (meth)acrylate monomers, (meth)acrylate oligomers, and mixtures thereof. As used herein, “monomer” or “oligomer” is any substance that can be converted into a polymer. The term “(meth)acrylate” refers to both acrylate and methacrylate compounds. In some cases, the polymerizable composition can comprise a (meth)acrylated urethane oligomer, (meth)acrylated epoxy oligomer, (meth)acrylated polyester oligomer, a (meth)acrylated phenolic oligomer, a (meth)acrylated acrylic oligomer, and mixtures thereof.

The polymerizable resin can be a radiation curable polymeric resin, such as a UV curable resin. In some cases, polymerizable resin compositions useful for the LCF of the present invention can include polymerizable resin compositions such as are described in U.S. Pat. No. 8,012,567 (Gaides et al.), to the extent that those compositions satisfy the index and absorption characteristics herein described.

The chemical composition and thickness of the base layer can depend on the end use of the LCF. In typical embodiments, the thickness of the base layer can be at least about 0.025 millimeters (25 microns) and can be from about 0.05 mm (50 microns) to about 0.25 mm (250 microns).

Useful base layer materials include, for example, styrene-acrylonitrile, cellulose acetate butyrate, cellulose acetate propionate, cellulose triacetate, polyether sulfone, polymethyl methacrylate, polyurethane, polyester, polycarbonate, polyvinyl chloride, polystyrene, polyethylene naphthalate, copolymers or blends based on naphthalene dicarboxylic acids, polyolefin-based material such as cast or orientated films of polyethylene, polypropylene, and polycyclo-olefins, polyimides, and glass. Optionally, the base layer can contain mixtures or combinations of these materials. In some embodiments, the base layer may be multi-layered or may contain a dispersed component suspended or dispersed in a continuous phase.

Examples of base layer material include polyethylene terephthalate (PET) and polycarbonate (PC). Examples of useful PET films include photograde polyethylene terephthalate, available from DuPont Films of Wilmington, Del. under the trade designation “Melinex 618”. Examples of optical grade polycarbonate films include LEXAN™ polycarbonate film 8010, available from GE Polymershapes, Seattle Wash., and Panlite 1151, available from Teijin Kasei, Alpharetta Ga. In some embodiments, the base layer is a PET film having a thickness of 75 microns. The base layer can have a matte or glossy finish.

Some base layers can be optically active and can act as polarizing materials. Polarization of light through a film can be accomplished, for example, by the inclusion of dichroic polarizers in a film material that selectively absorbs passing light. Light polarization can also be achieved by including inorganic materials such as aligned mica chips or by a discontinuous phase dispersed within a continuous film, such as droplets of light modulating liquid crystals dispersed within a continuous film. As an alternative, a film can be prepared from microtine layers of different materials. The polarizing materials within the film can be aligned into a polarizing orientation, for example, by employing methods such as stretching the film, applying electric or magnetic fields, and coating techniques.

Examples of polarizing films include those described in U.S. Pat. No. 5,825,543 (Ouderkirk et al.); U.S. Pat. No. 5,783,120 (Ouderkirk et al.); U.S. Pat. No. 5,882,774 (Jonza et al.); U.S. Pat. No. 5,612,820 (Shrenk et al.) and U.S. Pat. No. 5,486,949 (Shrenk et al.). The use of these polarizer films in combination with prismatic brightness enhancement film has been described, for example, in U.S. Pat. No. 6,111,696 (Allen et al.) and U.S. Pat. No. 5,828,488 (Ouderkirk et al.). Films available commercially are multilayer reflective polarizer films such as 3M™ Dual Brightness Enhancement Film “DBEF”, available from 3M Company.

In some embodiments, the base layer or cover film is a multilayer film that imparts a (e.g. color) wavelength shifting effect such as described in U.S. Pat. No. 8,503,122. Suitable color shifting films are described in U.S. Pat. No. 6,531,230 to Weber et al; incorporated herein by reference. Other suitable color shifting films include multilayer films generated by spin coating, blade coating, dip coating, evaporation, sputtering, chemical vapor deposition (CVD), and the like. Exemplary films include both organic and inorganic materials. Such films are described, for instance, in U.S. Pat. Nos. 7,140,741; 7,486,019; and 7,018,713.

The multilayer optical film can be an ultraviolet reflector, a blue reflector, a visible reflector, or an infrared reflector, as further described in U.S. Pat. No. 9,829,604, (Schmidt) dated Nov. 28, 2017.

In some embodiments, the multilayer optical film can be characterized as a UV reflective multilayer optical film (i.e. a UV reflector or UV mirror). A UV reflective multilayer optical film refers to a film having a reflectivity at normal incidence of at least 50, 60, 70, 80, or 90% for a bandwidth ranging from 290 nm to 400 nm. In some embodiments, the reflectivity at normal incidence for a bandwidth ranging from 290 nm to 400 nm is at least 91, 92, 93, 94, 95, 96, 97, or 98%. A UV reflective multilayer optical film can have low reflectivity and high transmission for visible light. For example, the transmission of visible light can be at least 85% or 90%.

In some embodiments, the multilayer optical film can be characterized as a UV-blue reflective multilayer optical film (i.e. a UV-blue reflector or UV-blue mirror). A UV-blue reflective multilayer optical film refers to a film having a reflectivity at normal incidence of at least 50, 60, 70, 80, or 90% for a bandwidth ranging from 350 nm to 490 nm. In some embodiments, the reflectivity at normal incidence for a bandwidth ranging from 350 nm to 490 nm is at least 91, 92, 93, 94, 95, 96, or 97%. The UV-blue reflective multilayer optical film can have low reflectivity and high transmission for visible light having wavelength greater than 500 nm. For example, the transmission of visible light having wavelength greater than 500 nm can be at least 85% or 90%.

In some embodiments, the multilayer optical film can be characterized as a near infrared reflective multilayer optical film (i.e. near infrared reflector or near infrared mirror). A near infrared reflective multilayer optical film refers to a film having a reflectivity at normal incidence of at least 50, 60, 70, 80, or 90% for a bandwidth ranging from 870 nm to 1100 nm. In some embodiments, the reflectivity at normal incidence for a bandwidth ranging from 870 nm to 1100 nm is at least 91, 92, 93, or 94%. In some embodiments, the film exhibits this same near infrared reflectivity at a 45 degree angle. The near infrared reflective multilayer optical film can have low reflectivity and high transmission for visible light. For example, the transmission of visible light can be at least 85%, 86%, 87% or 88%.

A visible light reflective multilayer optical film (e.g. visible reflector or visible mirror) refers to a film having a reflectivity at normal incidence of at least 50, 60, 70, 80, or 90% for a bandwidth ranging from 400 nm to 700 nm. In some embodiments, the reflectivity at normal incidence for a bandwidth ranging from 400 nm to 700 nm is at least 91, 92, 93, 94, 95, 96, 97, or 98%. The near infrared reflectivity properties of such broadband reflector are as previously described.

In other embodiments, a single multilayer optical film can reflect more than one bandwidth and may be considered a broadband reflector. For example, the multilayer optical film may be a visible and near infrared reflective multilayer optical film. Thus, such multilayer optical film has high reflectivity of both visible and near infrared bandwidths.

Additionally, two or more multilayer optical film mirrors, e.g. with different reflection bands, laminated together to broaden the reflection band. For example, a multilayer optical film visible reflector, such as previously described, can be combined with a UV, a UV-blue, and/or near infrared reflector. Various other combinations can be made as appreciated by one of ordinary skill in the art.

Alternatively, the microstructure-bearing article (e.g. microstructured film article 200 shown in FIG. 2) can be prepared by melt extrusion, i.e. casting a fluid resin composition onto a master negative microstructured molding surface (e.g. tool) and allowing the composition to harden. In this embodiment, the protrusions (e.g. light transmissive regions) are interconnected in a continuous layer to base layer 260. The individual protrusions (e.g. light transmissive regions) and connections therebetween generally comprises the same thermoplastic material. The thickness of the land layer (i.e. the thickness excluding that portion resulting from the replicated microstructure) is typically between 0.001 and 0.100 inches and preferably between 0.003 and 0.010 inches.

The thickness of the land layer can be lower when the microstructure-bearing article (e.g. microstructured film article 200 shown in FIG. 2) is prepared from the previously described cast and cure process. For example, the thickness of the land layer is typically at least 0.5, 1, 2, 3, 4, or 5 microns ranging up to 50 microns. In some embodiments, the thickness of the land layer is no greater than 45, 40, 35, 30, 25, 20, 15, or 10 microns. In one embodiment, the land layer is 8 microns.

Suitable resin compositions for melt extrusion are transparent materials that are dimensionally stable, durable, weatherable, and readily formable into the desired configuration. Examples of suitable materials include acrylics, which have an index of refraction of about 1.5, such as Plexiglas brand resin manufactured by Rohm and Haas Company; polycarbonates, which have an index of refraction of about 1.59; reactive materials such as thermoset acrylates and epoxy acrylates; polyethylene based ionomers, such as those marketed under the brand name of SURLYN by E. I. Dupont de Nemours and Co., Inc.; (poly)ethylene-co-acrylic acid; polyesters; polyurethanes; fluoropolymers; silicone polymers; ethylene vinyl acetate (EVA) copolymers, and cellulose acetate butyrates. Polycarbonates are particularly suitable because of their toughness and relatively higher refractive index.

In yet another embodiment, the master negative microstructured molding surface (e.g. tool) can be employed as an embossing tool, such as described in U.S. Pat. No. 4,601,861 (Pricone). The absorptive regions are generally formed by coating the surface of a microstructured film.

Various coating methods can be used including for example layer-by-layer coating (LbL), vapor deposition, sputtering, reactive sputtering and atomic layer deposition (ALD).

Light absorbing materials useful for forming light absorbing regions can be any suitable material that functions to absorb or block light at least in a portion of the visible spectrum. In typical embodiments, the light absorbing materials also absorb or block at least a portion of the UV and/or IR spectrum. Preferably, the light absorbing material can be coated or otherwise provided on the side walls of the light transmissive regions to form light absorbing regions in the LCF. Exemplary light absorbing materials include a black or other light absorbing colorant (such as carbon black or another pigment or dye, or combinations thereof). Other light absorbing materials can include particles or other scattering elements that can function to block light from being transmitted through the light absorbing regions. The light absorbing material can be organic, inorganic, or a combination thereof. Typically, the light absorbing material is organic at least in part.

When the light absorbing material (e.g. coating) includes particles, the particles have a median particle size D50 equal to or less than the thickness of the light absorbing material (e.g. coating) or in other words substantially less than the width of the absorptive regions W_(A).

The median particle size is generally less than 1 micron. In some embodiments, the median particle size is no greater than 900, 800, 700, 600, or 500 nm. In some embodiments, the median particle size is no greater than 450, 400, 350, 300, 250, 200, or 100 nm. In some embodiments, the median particle size is no greater than 90, 85, 80, 75, 70, 65, 60, 55, or 50 nm. In some embodiments, the median particle size is no greater than 30, 25, 20, or 15 nm. The median particle size is typically at least 1, 2, 3, 4, or 5 nanometers. The particle size of the nanoparticles of the absorptive regions can be measured using transmission electron microscopy or scanning electron microscopy, for example.

“Primary particle size” refers to the median diameter of a single (non-aggregate, non-agglomerate) particle. “Agglomerate” refers to a weak association between primary particles which may be held together by charge or polarity and can be broken down into smaller entities. As used herein “aggregate” with respect to particles refers to strongly bonded or fused particles where the resulting external surface area may be significantly smaller than the sum of calculated surface areas of the individual components. The forces holding an aggregate together are strong forces, for example covalent bonds, or those resulting from sintering or complex physical entanglement. Although agglomerated nanoparticles can be broken down into smaller entities such as discrete primary particles such as by application of a surface treatment; the application of a surface treatment to an aggregate simply results in a surface treated aggregate. In some embodiments, a majority of the nanoparticles (i.e. at least 50%) are present as discrete unagglomerated nanoparticles. For example, at least 70%, 80% or 90% of the nanoparticles (e.g. of the coating solution) are present as discrete unagglomerated nanoparticles.

The concentration of light absorbing nanoparticles is typically at least 10, 15, 20, 25, 30, 35, 40, 45, or 50 wt.-% of the total light absorptive region. In some embodiments, the concentration of light absorbing nanoparticles is at least 55, 60, 65, 70, or 75 wt.-% of the total light absorptive regions. The concentration of light absorbing nanoparticles can be determined by methods known in the art, such as thermogravimetric analysis.

In one embodiment, the method comprises applying a layer-by layer light absorptive coating to the surface of the microstructured film, i.e. the top surface and side walls of the protrusions and bottom surface of the channels.

In some embodiments, the plurality of layers disposed on the surface of the microstructured film comprise at least two layers deposited by what is commonly referred to as a “layer-by-layer self-assembly process”. This process is commonly used to assemble films or coatings of oppositely charged polyelectrolytes electrostatically, but other functionalities such as hydrogen bond donor/acceptors, metal ions/ligands, and covalent bonding moieties can be the driving force for film assembly. “Polyelectrolyte” means a polymer or compound with multiple ionic groups capable of electrostatic interaction. “Strong polyelectrolytes” possess permanent charges across a wide range of pH (e.g., polymers containing quaternary ammonium groups or sulfonic acid groups). “Weak polyelectrolytes” possess a pH-dependent level of charge (e.g. polymers containing primary, secondary, or tertiary amines, or carboxylic acids). Typically, this deposition process involves exposing the substrate having a surface charge, to a series of liquid solutions, or baths. This can be accomplished by immersion of the substrate into liquid baths (also referred to as dip coating), spraying, spin coating, roll coating, inkjet printing, and the like. Exposure to the first polyion (e.g. polyelectrolyte bath) liquid solution, which has charge opposite that of the substrate, results in charged species near the substrate surface adsorbing quickly, establishing a concentration gradient, and drawing more polyelectrolyte from the bulk solution to the surface. Further adsorption occurs until a sufficient layer has developed to mask the underlying charge and reverse the net charge of the substrate surface. In order for mass transfer and adsorption to occur, this exposure time is typically on the order of minutes. The substrate is then removed from the first polyion (e.g. bath) liquid solution, and then exposed to a series of water rinse baths to remove any physically entangled or loosely bound polyelectrolyte. Following these rinse (e.g. bath) liquid solutions, the substrate is then exposed to a second polyion (e.g. polyelectrolyte or inorganic oxide nanoparticle bath) liquid solution, which has charge opposite that of the first polyion (e.g. bath) liquid solution. Once again adsorption occurs, since the surface charge of the substrate is opposite that of the second (e.g. bath) liquid solution. Continued exposure to the second polyion (e.g. bath) liquid solution then results in a reversal of the surface charge of the substrate. A subsequent rinsing can be performed to complete the cycle. This sequence of steps is said to build up a one layer pair, also referred to herein as a “bi-layer” of deposition and can be repeated as desired to add further layer pairs to the substrate.

Some examples of suitable processes include those described in Krogman et al., U.S. Pat. No. 8,234,998; Hammond-Cunningham et al., US2011/0064936; and Nogueira et al., U.S. Pat. No. 8,313,798. Layer-by layer dip coating can be conducted using a StratoSequence VI (nanoStrata Inc., Tallahassee, Fla.) dip coating robot.

In one embodiment, the plurality of bi-layers deposited by layer-by-layer self-assembly is a polyelectrolyte stack comprising an organic polymeric polyion (e.g. cation) and counterion (e.g. anion) comprising a light absorbing material (e.g. pigment). At least a portion of the cation layers, anion layers, or a combination thereof comprise a light absorbing material (e.g. pigment) ionically bonded to the polyelectrolyte.

The thickness of a bi-layer and the number of bi-layers are selected to achieve the desired light absorption. In some embodiments, the thickness of a bi-layer, the number of bi-layers are selected to achieve the desired (e.g. absorption) optical properties using the minimum total thickness of self-assembled layers and/or the minimum number of layer-by-layer deposition steps. The thickness of each bi-layer typically ranges from about 5 nm to 350 nm. The number of bi-layers is typically at least 5, 6, 7, 8, 9, or 10. In some embodiments, the number of bilayers per stack is no greater than 150 or 100. The thickness of a stack is equivalent to the width of the absorptive regions W_(A), as previously described.

A light absorbing compound is dispersed within at least a portion of the polyelectrolyte layers. Various polyelectrolytes can be utilized including inorganic compounds, such as silica or silicate, as well as various phosphonocarboxylic acids and salts thereof (some of which are described in WO2015/095317; incorporated herein by reference.)

Polyelectrolyte organic polymers can be preferred since such materials can be more easily removed by reactive ion etching than inorganic materials.

Suitable polycationic organic polymers include, but are not limited to linear and branched poly(ethylenimine) (PEI), poly(allylamine hydrochloride), polyvinylamine, chitosan, polyaniline, polyamidoamine, poly(vinylbenzyltriamethylamine), polydiallyldimethylammonium chloride (PDAC), poly(dimethylaminoethyl methacrylate), poly(methacryloylamino)propyl-trimethylammonium chloride, and combinations thereof including copolymers thereof.

Suitable polyanionic organic polymers include, but are not limited to, poly(vinyl sulfate), poly(vinyl sulfonate), poly(acrylic acid) (PAA), poly(methacrylic acid), poly(styrene sulfonate), dextran sulfate, heparin, hyaluronic acid, carrageenan, carboxymethylcellulose, alginate, sulfonated tetrafluoroethylene based fluoropolymers such as Nafion®, poly(vinylphosphoric acid), poly(vinylphosphonic acid), and combinations thereof including copolymers thereof.

The molecular weight of the polyelectrolyte polymers can vary, ranging from about 1,000 g/mole to about 1,000,000 g/mole. In some embodiments, the molecular weight (Mw) of the (e.g. poly(acrylic acid)) negatively charged anionic layer ranges from 50,000 g/mole to 150,000 g/mole. In some embodiments, the molecular weight (Mw) of the (e.g. polydiallyldimethylammonium chloride) positively charged cationic layer ranges from 50,000 g/mole to 300,000 g/mole. In some embodiments, the molecular weight (Mw) of the (e.g. poly(ethyleneimine) positively charged cationic layer ranges from 10,000 g/mole to 50,000 g/mole.

At least one of the polyions (e.g. the polyanion or polycation) comprises a light absorbing material.

In order to be stable in water as a colloidal dispersion and impart polyionic groups, the light absorbing (e.g. pigment) particles typically further comprise an ionic surface treatment. In some embodiments, the surface treatment compound is anionic, such as in the case of sulfonate or carboxylate. The light absorbing (e.g. pigment) particles also function as the ionic binding group for the alternating polyelectrolyte layer.

Suitable pigments are available commercially as colloidally stable water dispersions from manufacturers such as Cabot, Clariant, DuPont, Dainippon and DeGussa. Particularly suitable pigments include those available from Cabot Corporation under the CAB-O-JET® name, for example 250C (cyan), 260M (magenta), 270Y (yellow) or 352K (black). The light absorbing (e.g. pigment) particles are typically surface treated to impart ionizable functionality. Examples of suitable ionizable functionality for light absorbing (e.g. pigment) particles include sulfonate functionality, carboxylate functionality as well as phosphate or bisphosphonate functionality. In some embodiments, surface treated light absorbing (e.g. pigment) particles having ionizable functionality are commercially available. For example, CAB-O-JET® pigments, commercially available from Cabot Corporation, sold under the trade names 250C (cyan), 260M (magenta), 270Y (yellow) and 200 (black), comprise sulfonate functionality. As yet another example, CAB-O-JET® pigments commercially available from Cabot Corporation, under the trade names 352K (black) and 300 (black), comprise carboxylate functionality.

When the light absorbing (e.g. pigment) particles are not pre-treated, the light absorbing (e.g. pigment) particles can be surface treated to impart ionizable functionality as known in the art.

Multiple light absorbing materials (e.g. pigments) may be utilized to achieve a specific hue or shade or color in the final product. When multiple light absorbing materials (e.g. pigments) are used, the materials are selected to ensure their compatibility and performance both with each other and with the optical product components.

In some embodiments, such as when the absorptive regions comprise carbon black, the light control film generally provides low transmission (e.g. less than 10%) at a viewing angle of 30 degrees for wavelengths ranging from 300 nm to 2400 nm. When the absorptive regions are colored, the light control film can exhibit a higher average transmission. For examples the transmission can be 10 to 30% at a viewing angle of 30 degrees for wavelengths ranging from 300 nm to 2400 nm. However, specific wavelength ranges can exhibit a lower transmission at the wavelength range of the color of the absorptive regions. In some embodiments, the transmission is less than 15% at a viewing angle of 30 degrees for wavelengths ranging from 300 nm to 550 nm. In some embodiments, the transmission is less than 5, 4, 3, 2, or 1% at a viewing angle of 30 degrees for wavelengths ranging from 600 nm to 750 nm.

In favored embodiments, the polyelectrolyte is prepared and applied to the microstructured surface as an aqueous solution. The term “aqueous” means that the liquid of the coating contains at least 85 percent by weight of water. It may contain a higher amount of water such as, for example, at least 90, 95, or even at least 99 percent by weight of water or more. The aqueous liquid medium may comprise a mixture of water and one or more water-soluble organic cosolvent(s), in amounts such that the aqueous liquid medium forms a single phase. Examples of water-soluble organic cosolvents include methanol, ethanol, isopropanol, 2-methoxyethanol, 3-methoxypropanol, 1-methoxy-2-propanol, tetrahydrofuran, and ketone or ester solvents. The amount of organic cosolvent typically does not exceed 15 wt-% of the total liquids of the coating composition. The aqueous polyelectrolyte composition for use in layer-by-layer self-assembly typically comprises at least 0.01 wt-%, 0.05 wt-% or 0.1 wt-% of polyelectrolyte and typically no greater than 5 wt-%, 4 wt-%, 3 wt-%, 2 wt-% or 1 wt-%.

In some embodiments, the aqueous solutions further comprise a “screening agent”, an additive that promotes even and reproducible deposition by increasing ionic strength and reducing interparticle electrostatic repulsion. Suitable screening agents include any low molecular weight salts such as halide salts, sulfate salts, nitrate salts, phosphate salts, fluorophosphate salts, and the like. Examples of halide salts include chloride salts such as LiCl, NaCl, KCl, CaCl₂, MgCl₂, NH₄Cl and the like, bromide salts such as LiBr, NaBr, KBr, CaBr₂, MgBr₂, and the like, iodide salts such as LiI, NaI, KI, CaI₂, MgI₂, and the like, and fluoride salts such as, NaF, KF, and the like. Examples of sulfate salts include Li₂SO₄, Na₂SO₄, K₂SO₄, (NH₄)₂SO₄, MgSO₄, CoSO₄, CuSO₄, ZnSO₄, SrSO₄, Al₂(SO₄)₃, and Fe₂(SO₄)₃. Organic salts such as (CH₃)₃CCl, (C₂H₅)₃CCl, and the like are also suitable screening agents.

Suitable screening agent concentrations can vary with the ionic strength of the salt. In some embodiments, the aqueous solution comprises (e.g. NaCl) screening agent at a concentration ranging from 0.01 M to 0.1M. The absorptive regions may contain trace amounts of screening agent.

After applying and drying the light absorbing coating to the (e.g. entire) surface of the microstructured film, the light absorbing coating is then removed from the top portions of the transmissive (e.g. protrusions) regions and also removed from the land regions, between the transmissive (e.g. protrusions) regions. It is appreciated that the LCF can have improved on-axis transmission (e.g. brightness) even when some of the light absorbing coating is retained.

Any suitable method can be used to selectively remove the light absorbing material from the top surface of the protrusions (e.g. light absorbing regions) and bottom surface of the channels.

In one embodiment, the light absorbing material is removed by reactive ion etching. Reactive ion etching (RIE) is a directional etching process utilizing ion bombardment to remove material. RIE systems are used to remove organic or inorganic material by etching surfaces orthogonal to the direction of the ion bombardment. The most notable difference between reactive ion etching; and isotropic plasma etching is the etch direction. Reactive ion etching is characterized by a ratio of the vertical etch rate to the lateral etch rate which is greater than 1. Systems for reactive ion etching are built around a durable vacuum chamber. Before beginning the etching process, the chamber is evacuated to a base pressure lower than 1 mTorr, 100 mTorr, 20 mTorr, 10 mTorr, or 1 mTorr. An electrode holds the materials to be treated and is electrically isolated from the vacuum chamber. The electrode may be a rotatable electrode in a cylindrical shape. A counter electrode is also provided within the chamber and may be comprised of the vacuum reactor walls. Gas comprising an etchant enters the chamber through a control valve. The process pressure is maintained by continuously evacuating chamber gases through a vacuum pump. The type of gas used varies depending on the etch process. Carbon tetrafluoride (CF₄), sulfur hexafluoride (SF₆), octafluoropropane (C₃F₈), fluoroform (CHF₃) boron trichloride (BCl₃), hydrogen bromide (HBr), chlorine, argon, and oxygen are commonly used for etching. RF power is applied to the electrode to generate a plasma. Samples can be conveyed on the electrode through plasma for a controlled time period to achieve a specified etch depth. Reactive ion etching is known in the art and further described in U.S. Pat. No. 8,460,568; incorporated herein by reference.

In some embodiments, the step of reactive ion etching results in the absorptive regions being narrower (less than the average width) near the bottom surface 311 of the channels. Removing the light absorbing material can result in a (e.g. slight) increase in the depth of the channels. Some of the light absorbing material may remain after etching.

After removing the light absorbing coating from the bottom surface of the channels, the channels can be filled with an organic polymeric material. In some embodiments, the organic polymeric material is a polymerizable resin composition and the method further comprising (e.g. radiation) curing the polymerizable resin. Typically, the same polymerizable resin used in the manufacture of the microstructured film is utilized for filling the channels. Alternatively, a different organic polymeric material (e.g. polymerizable resin composition) is used. When a different organic polymer material (e.g. polymerizable resin composition) is used, the composition is typically selected to be index matched to the light transmissive regions. By “index matched”, it is meant that the difference in refractive index between the filling material and transmissive regions is typically less than 0.1 or 0.005. Alternatively, the channels may be filled with a different organic polymeric material (e.g. polymerizable resin composition) having a difference in refractive index of greater than 0.1. In yet another embodiment, the channels are not filled with an organic polymeric material (e.g. polymerized resin). In this embodiment, the channels typically comprise air, having a refractive index of 1.0.

When the channels are filled with a cured polymerizable resin, the light control film may optionally include cover film 470 bonded to the microstructured film with adhesive 410. When the channels are filled with air, the adhesive film and cover film are typically included.

In yet another embodiment, layer 410 may be a topcoat rather than adhesive. In this embodiment, cover film 470 may not be present.

FIG. 4 shows an LCF 400 that further includes an optional cover film 470 that can be the same, or different than, base layer 260. Optional cover film 470 can be bonded to the microstructured surface with an adhesive 410. Adhesive 410 can be any optically clear adhesive, such as a UV-curable acrylate adhesive, a transfer adhesive, and the like.

Alternatively, the cover film can be contacted with the polymerizable resin utilized to fill the channels (e.g. back-filling resin). The back-filling resin is cured while in contact with the cover film, thereby bonding the cover film.

One or more of the surfaces of the cover film can optionally be primed or otherwise treated to promote adhesion with the adhesive or back-filling resin.

In typical embodiment, the thickness of the cover film can be at least about 0.025 millimeters (25 microns) and can be from about 0.05 mm (50 microns) to about 0.25 mm (250 microns). In some embodiments, the cover film is a multilayer wavelength (e.g. color) shifting film as previously described.

The LCF may further comprise other coatings typically provided on the exposed surface. Various hardcoats, antiglare coatings, antireflective coatings, antistatic, and anti-soiling coatings are known in the art. See for example U.S. Pat. Nos. 7,267,850; 7,173,778, PCT Publication Nos. WO2006/102383, WO2006/025992, WO2006/025956 and U.S. Pat. No. 7,575,847.

FIG. 5 shows a perspective schematic of a backlit display 500 according to one embodiment. Backlit display 500 includes an LCF 530 comprising transmissive regions 540 and absorptive regions 550 as previously described. Such LCF has a polar cut-off viewing angle θP, as previously described, of light leaving an output surface 590 of LCF 530. Backlit display 500 includes a light source 510 configured to transmit light through LCF 530, through an image plane 520, such as an LCD panel, and on to a viewer 595. The viewing angle at which the brightness is a maximum, can depend on the polar cut-off viewing angle as previously described.

Backlit display 500 can also include an optional brightness enhancement film 560 and a reflective polarizer film 570 to further improve the brightness and uniformity of the display. Brightness enhancement film can be a prism film, such as 3M™ Brightness Enhancement Film “BEF” or Thin Brightness Enhancement Film “TBEF”, available from 3M Company. Reflective polarizer film 570 can be a multilayer optical film, such as 3M™ Dual Brightness Enhancement Film “DBEF”, available from 3M Company, St. Paul, Minn. Brightness enhancement film 560 and reflective polarizer film 570, if included, can be positioned as shown in FIG. 5.

In other embodiments, the light control film comprising transmissive regions and absorptive regions, as previously described, can be bonded to an emissive (e.g. an organic light emitting diode, or OLED) display.

In some embodiments, the LCF described herein (i.e. a first LCF) can be combined with a second LCF. In some embodiments, the second LCF may be a LCF (e.g. privacy film) such described in U.S. Pat. Nos. 6,398,370; 8,013,567; 8,213,082; and 9,335,449. In other embodiments, the second LCF is an LCF as described herein (e.g. wherein the light absorbing regions have an aspect ratio of at least 30). The first and second LCFs can be stacked in various orientations.

In one embodiment, the first and second light control films are positioned such that the absorptive regions of the first LCF are parallel and typically coincident with the absorptive regions of the second LCF. In another embodiment, the first and second light control films are positioned such that the absorptive regions of the first LCF are orthogonal with the absorptive regions of the second LCF. The first and second light control films can also be positioned such that the absorptive regions range from being parallel to orthogonal with each other at a viewing angle of 0 degrees.

In some embodiments, the combination of first and second LCF has a relative transmission (e.g. brightness) of at least 60, 65, 70, 75, 80, 85, or 90% at a viewing angle of 0 degrees. In some embodiments, the relative transmission (e.g. brightness) at a viewing angle of +30 degrees, −30 degrees, or the average of +30 and −30 degrees is less than 25, 20, 15, 10, or 5%. In some embodiments, the average relative transmission (e.g. brightness) for viewing angles ranging from +35 to +80 degrees, −35 degrees to −85 degrees, or the average of these ranges is less than 10, 9, 8, 7, 6, 5, 4, 3, 2, or 1%.

In some embodiments, this combination of LCF has a relative transmission (e.g. brightness) of at least 60, 65, 70, 75, 80, 85, or 90% at a viewing angle of 0 degrees. In some embodiments, the relative transmission (e.g. brightness) at a viewing angle of +30 degrees, −30 degrees, or the average of +30 and −30 degrees is less than 25, 20, 15, 10, or 5%.

When the channels are filled with air, the relative transmission (e.g. brightness) at higher viewing angles can be lower, and thus the film can exhibit improved privacy.

The light control films described herein are particularly useful as a component of a display device as a so-called hybrid privacy filter. The hybrid privacy filter may be used in conjunction with a display surface, wherein light enters the hybrid privacy filter on the input side of the light control film and exits the hybrid privacy filter or film stack at the color shifting film. A great number of electronic devices with displays may be used in conjunction with the present invention including laptop monitors, external computer monitors, cell phone displays, televisions, smart phones, automotive center information displays, automotive driver information displays, automotive side mirror displays (also referred to as e-mirrors), consoles, or any other similar LCD, OLED, micro-LED, or mini-LED based display. An additional benefit to applying hybrid privacy filters to a display is for contrast enhancement.

Other types of backlit display imaging devices are also contemplated, including non-electronic displays such as sunglasses, document coversheets, console switches in auto and aviation applications, airplane cockpit controls, helicopter cockpit controls, windows and any number of others.

In further embodiments, the light control film described herein can be useful as coverings for glass and solar panels. For instance, the light control films may be laminated onto or within fenestrations. The fenestrations may be selected from a glass panel, a window, a door, a wall, and a skylight unit. These fenestrations may be located on the outside of a building or on the interior. They may also be car windows, train windows, airplane passenger windows, ATMs, or the like. Advantages of incorporating these film stacks into fenestrations include reduced IR transmission (which may lead to increased energy savings), ambient light blocking, privacy, and decorative effects.

In some embodiments, the light control films (LCFs) described herein may be part of an optical communication system. The “optical communication system” as referred to herein is a system that is for communication of light over a distance from a light source through a disclosed LCF to a target, where the target may include a detector or human eye and the light source may include ambient light. Exemplary light sources include a light emitting diode (LED) that emit UV, visible or NIR, a laser light source including VCSEL (vertical cavity surface emitting laser), a halogen light source, an incandescent light source, a metal halide light source, a tungsten light source, a mercury vapor light source, a short arc xenon light source, or the sun (solar). In some cases, the LCFs disclosed herein may be part of an optical communication system with a detector system. In some cases, the detector system may provide various types of outputs, such as electronic signals, when receiving light passing through the LCF of the optical communication system. A detector system includes a detector that is sensitive to wavelengths in a detection wavelength range and an LCF disposed on the detector.

In some embodiments, the detector is or includes a photovoltaic device. The detector may be configured to detect solar radiation, for example, to charge a battery. In such cases, the detector is or may include a solar battery, a solar cell, silicone photodiode, or a solar detector. In some cases, the detector may be the detector in a (e.g. visible or near infrared) camera for detecting and/or recording an image. In some cases, the detector may be a in a camera or camera system. Other detectors include CMOS (complementary metal-oxide semiconductor) and CCD (charge-coupled device) detectors. Typical applications of light detectors (also referred to herein as sensors) include gesture recognition, iris recognition, face recognition, remote control and autonomous vehicles, ambient light sensor, proximity sensor, heart rate, blood oxygen, glucose or other biological sensing, 3D depth camera with time of flight or structured light, security camera.

In some cases, the light control films (LCFs) disclosed herein may be part of an optical communication system including an optical construction combined with, for example, a window as shown in FIG. 7. In this example, the LCF 600 is a part of an optical construction 601 with a natural light source such as sun light 690. In particular, FIG. 7 shows an exemplary application of a disclosed LCF applied to a window to an enclosure, such as a building, a house or a vehicle. LCF 600 may be disposed on a window substrate 675 of a building, a house, a car or any enclosure 670. The LCF 600 includes an optical film 650 that includes a plurality of spaced apart first absorptive regions 630 and an optional second (e.g. cover film) region 640 adjacent at least a portion of at least one first region 630. The first regions 630 comprise a first material absorptive material 632 and the second region 640 may include a second material 642.

In a favored embodiment, the LCF window film exhibits high transmission of visible light in combination with low transmission of bother UV light and NIR light.

The transmission of ultraviolet light and infrared light by the first absorptive regions 630 vary as a function of the incidence angle of the light. In particular, when the sun light 690 is incident perpendicularly to the LCF 600, the infrared light and the visible light may both be transmitted through the optical film 650. However, as the incidence angle of the light from the sun 690 increases, the amount of the infrared light transmitted through the LCF 600 decreases until the incidence angle reaches the viewing angle θP from which point on substantially all the infrared light is blocked by the first material 632. That is, during the morning hours when the infrared portion of the sun light 690 is relatively small and the sun light 690 is incident on the window at normal incidence angle, most of the infrared light may be transmitted by the LCF 600. On the other hand, close to noon, when the infrared portion of the sun light 690 is relatively large and the incident angle of the sun light 690 is increased close to or beyond the viewing angle 20 v of the LCF 600, very little of the incident infrared light is transmitted by the LCF 600 and finally blocked so that the viewer or resident 677 inside of the building or house 670 may not be exposed to the hot infrared light. Thus, the LCF 600 can reduce exposure to ultraviolet and infrared light.

FIG. 8 schematically shows the relation between the detector sensitivity and wavelength illustrating that the detector is sensitive to wavelengths in the detection wavelength range. As shown in FIG. 8, each first region of a disclosed LCF may have a substantially high transmission in a predetermined first wavelength range “A”, a substantially low transmission in a predetermined second wavelength range “B”, and a substantially high transmission in a predetermined third wavelength range “C”, where the second wavelength range B is disposed between the first and third wavelength ranges A and C, respectively. In some cases, the second wavelength range B is about 20 nm wide from a first wavelength 712 to a second wavelength 714 and centered on a laser visible emission wavelength, the first wavelength range A is from about 400 nm to about the first wavelength 712, and the third wavelength range C is from about the second wavelength 714 to about 1400 nm. The laser visible emission wavelength may be at least one of 442 nm, 458 nm, 488 nm, 514 nm, 632.8 nm, 980 nm, 1047 nm, 1064 nm, and 1152 nm. In other examples, the laser visible emission wavelength is in a range from about 416 nm to about 1360. In further examples, the LCF further may include a plurality of spaced apart second regions alternating with the plurality of first regions and each second region may have a substantially high transmission in each of the predetermined first, second and third wavelength ranges. In other example, each second region may have a substantially low transmission in either/both the predetermined first or/and third wavelength ranges. In some cases, the LCF has a viewing angle of less than about 60 degrees, or 50 degrees, or 40 degrees, or 30 degrees, or 20 degrees in the predetermined second wavelength range.

In another exemplary application, the LCFs disclosed herein may be a part of an optical communication system with a separate light source such as laser light source as shown in FIG. 9. In particular, FIG. 9 shows an exemplary application where a LCF is applied to a plane or an aircraft laser strike defense system to block an incoming or incident light in a predetermined wavelength range. An LCF 800 may be attached to, for example, a plane, an airplane or aircraft 870, etc. and desirably, attached to a surface (such as a window) of the plane, airplane or aircraft 870. The LCF 800 includes an optical film 850 that includes a plurality of spaced apart first adsorptive regions 830 and optional second (e.g. cover film) region 840 adjacent at least a portion of at least one of the first regions 830. The first regions 830 comprise a first absorptive material 832 and the second region 840 includes a second material 842.

When laser light 891 is incident on the LCF 800, the second (e.g. cover film) material 842 absorbs or/and reflects at least a part of ultraviolet light and infrared wavelength ranges regardless of the incidence angle of the light 891. Furthermore, the second (e.g. cover film) region 840 transmits in a range of the visible wavelengths that include the laser light 891 wavelength, but the transmission of the visible light through the first regions 830 vary as a function of an incidence angle of the light. When the light is incident perpendicularly to the surface of the LCF 800, the visible light can be transmitted through the optical film 850. However, outside viewing angle, θP (refer to FIG. 1b ), the visible light is blocked by the first absorptive material 832 in the first regions 830. Therefore, when using the LCF 800 on the plane or aircraft 870, the visible light from the laser light 891 within the viewing angle θP can be transmitted by the LCF 800 but the ultraviolet light and the infrared light from the laser light 891 may not be transmitted by the LCF 800 or only a restricted amount of the ultraviolet light and infrared light, desirably less than about 10% the ultraviolet light and infrared light respectively may be transmitted by the LCF 800. The visible light can be transmitted by the LCF 800 as a function of an incidence angle including a wavelength of the light. Laser striker 878 may attack the plane or aircraft 870, for example, using a green laser 890 in order to obstruct a view of a pilot 877. Normally, the wavelength of the green color is about from 495 nm to 570 nm. Therefore, when LCF 800 includes a first absorptive material 832 that blocks the range of the wavelengths from 495 nm to 570 nm of the light, pilot 877 on the plane or aircraft 870 is not affected by the green laser attack from the laser striker 878 on the ground.

In some cases, the disclosed light control films (LCFs) may be utilized in combination with retroreflectors. For example, FIG. 10 shows a retroreflective system 1101 that includes a retroreflective sheet 1190 for retroreflecting light, and a LCF 1100 disposed on the retroreflective sheet 1190. In general, retroreflector sheet 1190 is configured to retroreflect light for a range of incident wavelengths and angles. For example, retroreflector sheet 1190 may be configured to retroreflect light for different incident wavelengths λ₁ and λ₂ and different incident angles α and α′. The addition of LCF 1100 results in system 1101 having modified retroreflective properties. For example, for a larger angle α and a smaller angle α′, the viewing angle θP of LCF 1100 may be such that for the smaller incident angle α′, LCF 1100 substantially transmits light at both wavelengths λ₁ and λ₂, but for the larger incident angle α, LCF may substantially transmit light having wavelength λ₁ and substantially absorb light having wavelength λ₂. For example, in some cases, the viewing angle θP of LCF 1100 may be greater than a′ and less than a. As another example, retroreflective system 1101 is so configured that for a first wavelength λ₁, lights 810 and 810′ incident on LCF 1100 at corresponding first and second angles of incidence α′ and α, are both retroreflected as respective retroreflected lights 812 and 812′. Furthermore, for a second wavelength λ₂, light 820 incident on the LCF at the first incidence angle α′ is retroreflected at retroreflected light 822, but light 820′ incident on the LCF at the second incidence angle α is not retroreflected. In such cases, light 820′ is absorbed by LCF 1100 when it is first incident on the LCF and, in some cases, after it is partially transmitted by the LCF and retroreflected by the retroreflective sheet. In some cases, LCF 1100 includes a larger first viewing angle for the first wavelength and a smaller viewing angle for the second wavelength. In some cases, the first angle of incidence α′ is substantially equal to zero relative to a line 801 normal to a plane of the LCF 1100. In some cases, retroreflective sheet 1190 includes microsphere beads 610 for retroreflecting light. In some cases, retroreflective sheet 1190 includes corner cubes 620 for retroreflecting light. In some cases, LCF 1100 includes a plurality of spaced apart first regions 1130, where each first region 1130 has a substantially low transmission at the second wavelength λ₂, but not at the first wavelength λ₁.

In another case, the LCF can be used in a part of an optical communication system with a sensor, more specifically a pulse sensor applied to a wrist watch as shown in FIG. 11. In particular, FIG. 11 shows an exemplary application of an LCF applied to a wrist watch with a pulse sensor. An LCF 1200 may be attached to a wearable wrist watch 1280 or any wearable device and desirably, attached to a surface of the wearable watch 1280. The LCF 1200 includes an optical film 1250 that includes a plurality of first absorptive regions 1230 and optionally a second (e.g. cover film) region 1240 adjacent at least a portion of a least one first regions 1230. The first regions 1230 comprise a first absorptive material 1232 and the second region 1240 may include a second material 1242. The first material 1232 may be any suitable material such that the first material 1232 is spectrally selective in at least a part of visible light range from the light source, for example, LED 1290 and the second material 1242 is spectrally selective in at least a part of at least one of ultraviolet light and infrared light ranges from the LED 1209. More desirably, the second material 1242 is spectrally selective in both ranges in the ultraviolet light and infrared light ranges. When using the LCF 1200, noises like ultraviolet light and infrared light from the perspective of a pulse sensor 1285 are absorbed through the second material 1242 regardless of the incidence angle of the light from light source such as sun light 1295 or LED 1290. The transmission of the ultraviolet light and infrared light from the light source passing through the second region 1240 is uniform and desirably, less than about 10%, regardless of the incidence angle of the light. However, the second region 1240 transmits a range of the visible light from LED 1290 but the transmission of the visible light through the first regions 1230 varies as a function of the incidence angle of the light. When the light from LED 1290 is incident perpendicularly on the surface of the LCF 1200, the visible light may be transmitted through the optical film 1250. However, the first material 1232 may block or decrease the sun light 1295 or ambient visible light from other light sources that are incident with relatively high incidence angle to the wrist 777 of the person wearing the device so that the LCF 1200 may improve signal (mainly visible light from LED that is incident within a viewing angle) to noise (for example, ultraviolet light or infrared light or ambient visible light from, for example, sunlight, other ambient light source that is incident outside viewing angle) ratio.

The present description should not be considered limited to the particular examples described herein, but rather should be understood to cover all aspects of the description as fairly set out in the attached claims. Various modifications, equivalent processes, as well as numerous structures to which the present description can be applicable will be readily apparent to those of skill in the art to which the present description is directed upon review of the instant specification. The foregoing description can be better understood by consideration of the embodiments shown by the testing results and examples that follow.

EMBODIMENTS OF THE INVENTION Embodiment 1

A light control film, comprising a light input surface and a light output surface opposite the light input surface; alternating transmissive regions and absorptive regions disposed between the light input surface and the light output surface, wherein the absorptive regions have an aspect ratio of at least 30 and the alternating transmissive region and absorptive regions have a relative transmission at a viewing angle of 0 degrees of at least 75%.

Embodiment 2

The light control film of embodiment 1 wherein the absorptive regions have a width parallel to light input surface and a height orthogonal to the light input surface.

Embodiment 3

The light control film of embodiments 1-2 wherein the alternating transmissive region and absorptive regions have a relative transmission at a viewing angle of +30 degrees or −30 degrees of less than 50, 45, 40, 35, 30, 25, 20, 10%, or 5%.

Embodiment 4

The light control film of embodiments 1-3 wherein the alternating transmissive region and absorptive regions have an average relative transmission for viewing angles ranging from +35 to +80 degrees or an average relative transmission for viewing angles ranging from −35 to −80 degrees of less than 10, 9, 8, 7, 6, 5, 4, 3, or 2%.

Embodiment 5

The light control film of embodiments 1-4 wherein the transmissive regions have a wall angle less than 5, 4, 3, 2, 1 or 0.1 degrees.

Embodiment 6

The light control film of embodiments 1-5 wherein the transmissive regions and absorptive regions have a height ranging from 50 to 200 microns.

Embodiment 7

The light control film of embodiments 1-6 wherein the absorptive region has an average width no greater than 5, 4, 3, 2, 1, 0.5, 0.25, or 0.10 microns.

Embodiment 8

The light control film of embodiments 1-7 wherein the absorptive regions have an aspect ratio of at least 50, 100, 200, 300, 400, 500, 600, 700, 800 or 1000.

Embodiment 9

The light control film of embodiments 1-8 wherein the absorptive regions have an average pitch of 10 to 200 microns.

Embodiment 10

The light control film of embodiments 1-9 wherein the transmissive regions have an aspect ratio of at least 2, 3, 4, 5, 6, 7, 8, 9, or 10.

Embodiment 11

The light control film of embodiments 1-10 wherein the absorptive regions comprise an organic light absorbing material.

Embodiment 12

The light control film of embodiments 1-11 wherein the absorptive regions comprise light-absorbing particles having a median particle size less than 500 nanometers.

Embodiment 13

The light control film of embodiments 1-12 wherein the absorptive regions comprise at least 25 wt.-% of light-absorbing particles.

Embodiment 14

The light control film of embodiments 1-13 wherein the absorptive regions comprise polyelectrolytes.

Embodiment 15

The light control film of embodiments 1-14 wherein the transmissive regions comprise a radiation cured (meth)acrylate polymer.

Embodiment 16

The light control film of embodiments 1-15 wherein the alternating transmissive regions and absorption region are disposed on a base layer.

Embodiment 17

The light control film of embodiments 1-16 wherein the light control film further comprises a cover film.

Embodiment 18

The light control film of embodiments 1-16 wherein the light control film has a relative transmission at a viewing angle of 0 degrees of at least 75%.

Embodiment 19

A light control film comprising a first light control film according to claim 1 disposed upon a second light control film.

Embodiment 20

The light control film of claim 19 wherein the second light control film is according to claim 1 and the first and second light control films are positioned such that the absorptive regions range from being parallel to orthogonal with each other at a viewing angle of 0 degrees.

Embodiment 21

The light control film of claim 20 wherein the second light control film is according to claim 1 and the first and second light control films are positioned such that the absorptive regions are coincident with each other at a viewing angle of 0 degrees.

Embodiment 22

The light control film of embodiments 1-21 wherein the transmission is for a wavelength range of 400 to 700 nm.

Embodiment 23

A microstructured film, comprising:

a light input surface and a light output surface opposite the light input surface; alternating transmissive regions and absorptive regions disposed between the light input surface and the light output surface, wherein the absorptive regions have an aspect ratio of at least 30 and comprise an organic light absorptive material.

Embodiment 24

The microstructured film of claim 23 wherein the microstructured film is further characterized by any one or combination of embodiments 2-22.

Embodiment 25

A microstructured film, comprising:

a light input surface and a light output surface opposite the light input surface; alternating transmissive regions and absorptive regions disposed between the light input surface and the light output surface, wherein the absorptive regions comprise a plurality of particles having a median particle size of less than 100 nanometers.

Embodiment 26

A microstructured film comprising:

a light input surface and a light output surface opposite the light input surface; alternating transmissive regions and absorptive regions disposed between the light input surface and the light output surface, wherein the absorptive regions comprise a polyelectrolyte.

Embodiment 27

The microstructured film of embodiments 25-26 wherein the absorptive regions have an aspect ratio of at least 30.

Embodiment 28

The microstructured film of embodiments 25-27 wherein the microstructured film is further characterized by any one or combination of embodiments 2-22.

Embodiment 29

A method of making a light control film comprising:

providing a microstructured film comprising a plurality of light transmissive regions alternated with channels, wherein the microstructured film has a surface defined by a top surface and side walls of the light transmissive regions and a bottom surface of the channels; applying an organic light absorptive material to the surface, and removing at least a portion of the light absorptive coating from the top surface of the light transmissive regions and bottom surface of the channels.

Embodiment 30

The method of claim 29 wherein the organic light absorptive material comprises polyelectrolytes.

Embodiment 31

The method of embodiments 29-30 wherein the organic light absorption material comprises a plurality of light absorbing particles.

Embodiment 32

The method of embodiments 29-31 wherein the light absorbing particles have an average particle size of less than 500 nm.

Embodiment 33

The method of embodiments 29-32 wherein the step of applying the light absorptive material comprises layer-by-layer self-assembly.

Embodiment 34

The method of embodiments 29-33 wherein the step of removing the at least a portion of the light absorptive coating comprises reactive ion etching.

Embodiment 35

The method of embodiments 29-34 further comprising filling the channel with an organic polymeric material.

Embodiment 36

The method of claim 35 wherein the organic polymeric material comprises a polymerizable resin and the method further comprising curing the polymerizable resin.

Embodiment 37

A method of making a microstructured film comprising:

providing a microstructured film comprising a plurality of light transmissive regions alternated with channels, wherein the microstructured film has a surface defined by a top surface and side walls of the light transmissive regions and a bottom surface of the channels; applying a light absorptive material to the surface by layer-by-layer self-assembly; removing at least a portion of the light absorptive coating from the top surface of the light transmissive regions and bottom surface of the channels.

Embodiment 38

The method of claim 37 wherein the material is a light absorptive material.

Embodiment 39

The method of embodiments 37-38 wherein method further comprises removing at least a portion of the material from the top surface of the protrusions and bottom surface of the channels.

Embodiment 40

The method of embodiments 37-39 wherein the method is further characterized by any one or combination of embodiments 30-36.

Embodiment 41

A light detection system, including:

a light source configured to emit light having a first spectral profile along a first direction and a second spectral profile along a different second direction; a detector sensitive to wavelengths in a detection wavelength range; a light control film according to embodiments 1-28 disposed on the light source or detector for receiving and transmitting light emitted by the light source.

Embodiment 42 The light detection system of embodiment 41 wherein the light source comprises a light emitting diode (LED), a laser light source, a halogen light source, a metal halide light source, a tungsten light source, a mercury vapor light source, a short arc xenon light source, or the sun.

Embodiment 43

The light detection system of embodiments 41-42 wherein the detector comprises a photovoltaic device, a solar battery, a solar cell, a camera.

Embodiment 44

The light detection system of embodiments 41-43 wherein the light control film is disposed on to the light source and the detector is remote.

Embodiment 45

The light detection system of embodiments 41-43 wherein the light control film is disposed on to the detector and the light source is remote.

Embodiment 46

The light detection system of embodiments 41-45 wherein the light detection system is a vehicle sensor.

Embodiment 47

The light detection system of embodiments 41-46 wherein the light control film is disposed on a retroreflective sheet.

Embodiment 48

The light detection system of embodiments 47 wherein retroreflective sheet comprises at least one of microsphere beads and corner cubes.

EXAMPLES

Unless otherwise noted, all parts, percentages, ratios, etc., in the examples and in the remainder of the specification are by weight. Unless otherwise noted, all chemicals were obtained from, or are available from, chemical suppliers such as Sigma-Aldrich Co., St. Louis, Mo.

The following is a list of materials used throughout the Examples, as well as their brief descriptions and origins.

The components of Resin A used in the cast-and-cure microreplication process (Preparative Example 1) as well as the index-matched backfill material in Examples 2 and Examples 4-8 are listed in Table 1 below. The raw materials for the layer-by-layer coating are listed in Table 2 below. The raw materials for reactive ion etching are listed in Table 3 below.

TABLE 1 Raw materials for Resin A Material Abbreviation Available From Aliphatic urethane diacrylate Photomer BASF Viscosity 5900 mPa · s at 60° C. 6010 Tensile Strength 2060 psi Tg = −7° C. Ethoxylated (10) bisphenol A SR602 Sartomer diacrylate (Exton, PA) Ethoxylated (4) bisphenol A SR601 Sartomer diacrylate (Exton, PA) Trimethylolpropane triacrylate TMPTA Cytec Industries (Woodland Park, NJ) Phenoxyethyl Acrylate PEA Eternal Chemical (Etermer Co., Ltd., 2010) Kaohsiung, Taiwan 2-Hydroxy-2- Darocur BASF Corporation methylpropiophenone 1173 (Florham Park, New photoinitiator Jersey) Diphenyl(2,4,6- TPO BASF Corporation trimethylbenzoyl)phosphine (Florham Park, New oxide photoinitiator Jersey) Irgacure 1035 anti-oxidant 11035 BASF Corporation (Florham Park, New Jersey)

TABLE 2 Raw materials for the layer-by-layer coatings Material Abbreviation Source Poly(diallyl-dimethyl PDAC Sigma-Aldrich Co. ammonium chloride), (St. Louis, Missouri) molecular weight 100-200K Polyethylenimine, molecular PEI Sigma-Aldrich Co. weight 25K (St. Louis, Missouri) Polyacrylic acid, molecular PAA Dow Chemical weight 100K, Accumer ™ Company 1510 (Midland, Michigan) CAB-O-JET ® 200 carbon COJ200 Cabot Corporation black nano-pigment, 130 nm (Boston, Massachusetts) diameter, sulfonate functionalized CAB-O-JET ® 250C cyan COJ250C Cabot Corporation nano-pigment, 91 nm (Boston, Massachusetts) diameter, sulfonate functionalized CAB-O-JET ® 260M COJ260M Cabot Corporation magenta nano-pigment, (Boston, Massachusetts) 105 nm diameter, sulfonate functionalized CAB-O-JET ® 352K COJ352K Cabot Corporation carbon black nano-pigment, (Boston, Massachusetts) 70-80 nm diameter, carboxylate functionalized Sodium chloride NaCl Sigma-Aldrich Co. (St. Louis, Missouri) Sodium hydroxide NaOH Avantor Performance (1M in water) Materials (Central Valley, PA)

TABLE 3 Raw materials for reactive ion etching Material Abbreviation Source Oxygen O₂ Oxygen Service Company (UHP compressed gas) (St Paul, Minnesota) Argon Ar Oxygen Service Company (UHP compressed gas) (St Paul, Minnesota)

Preparative Example 1 (PE1): Preparation of “Square Wave” Microstructured Film

A diamond (29.0 μm tip width, 3° included angle, 87 μm deep) was used to cut a tool having a plurality of parallel linear grooves. The grooves were spaced apart by a pitch of 62.6 microns.

Resin A was prepared by mixing the materials in Table 4 below.

TABLE 4 Composition of Resin A used to make microstructured film Material Parts by Weight Photomer 6010 60 SR602 20 SR601 4.0 TMPTA 8.0 PEA (Etermer 2010) 8.0 Darocur 1173 0.35 TPO 0.10 I1035 0.20

A “cast-and-cure” microreplication process was carried out with Resin A and a tool, as described above. The line conditions were: resin temperature 150° F., die temperature 150° F., coater IR 120° F. edges/130° F. center, tool temperature 100° F., and line speed 70 fpm, Fusion D lamps (available from Fusion UV Systems, Gaithersburg, Md., with peak wavelength at 385 nm, were used for curing and operated at 100% power. The resulting microstructured film comprised a plurality of protrusions (e.g. light transmissive regions) separated by channels as illustrated in FIG. 2. The base layer 260 was PET film (3M, St. Paul, Minn.), having a thickness of 2.93 mils (74.4 microns). The side of the PET film that contacts the resin was primed with a thermoset acrylic polymer (Rhoplex 3208 available from Dow Chemical, Midland, Mich.). The land layer (L) of the cured resin had a thickness of 8 microns. The microstructured film is a topographical inverse of the tool such that the protrusions of the microstructured film are a negative replication of the grooves of the tool. The protrusions have a wall angle of 1.5 degrees resulting in the protrusions being slightly tapered (wider at the light input surface and narrower at the light output surface). The channels of the microstructured film are a negative replication of the uncut portions of the tool between the grooves.

Method for Making Layer-by-Layer Self-Assembled Coatings on Microstructured Film

Layer-by-layer self-assembled coatings were made using an apparatus purchased from Svaya Nanotechnologies, Inc. (Sunnyvale, Calif.) and modeled after the system described in U.S. Pat. No. 8,234,998 (Krogman et al.) as well as Krogman et al. Automated Process for Improved Uniformity and Versatility of Layer-by-Layer Deposition, Langmuir 2007, 23, 3137-3141.

The apparatus comprises pressure vessels loaded with the coating solutions. Spray nozzles with a flat spray pattern (from Spraying Systems, Inc., Wheaton, Ill.) were mounted to spray the coating solutions and rinse water at specified times, controlled by solenoid valves. The pressure vessels (Alloy Products Corp., Waukesha, Wis.) containing the coating solutions were pressurized with nitrogen to 30 psi, while the pressure vessel containing deionized (DI) water was pressurized with air to 30 psi. Flow rates from the coating solution nozzles were each 10 gallons per hour, while flow rate from the DI water rinse nozzles were 40 gallons per hour. The substrate to be coated was adhered at the edges with epoxy (Scotch-Weld epoxy adhesive, DP100 Clear, 3M Company, St. Paul, Minn.) to a glass plate (12″×12″×⅛″ thick) (Brin Northwestern Glass Co., Minneapolis, Minn.), which was mounted on a vertical translation stage and held in place with a vacuum chuck. In a typical coating sequence, the polycation (e.g., PDAC) solution was sprayed onto the substrate while the stage moved vertically downward at 76 mm/sec. Next, after a dwell time of 12 sec, the DI water was sprayed onto the substrate while the stage moved vertically upward at 102 mm/sec. The substrate was then dried with an airknife at a speed of 3 mm/sec. Next, the polyanion (e.g., pigment nanoparticles) solution was sprayed onto the substrate while the stage moved vertically downward at 76 mm/sec. Another dwell period of 12 sec was allowed to elapse. The DI water was sprayed onto the substrate while the stage moved vertically upward at 102 mm/sec. Finally, the substrate was then dried with an airknife at a speed of 3 mm/sec. The above sequence was repeated to deposit a number of “bi-layers” denoted as (Polycation/Polyanion)_(n) where n is the number of bi-layers. The coated substrate (e.g. polymer film) was peeled off of the glass substrate prior to subsequent processing.

Method for Reactive Ion Etching Microstructured Film

Reactive ion etching (RIE) was performed in a parallel plate capacitively coupled plasma reactor. The chamber has a central cylindrical powered electrode with a surface area of 18.3 ft². After placing the microstructured film on the powered electrode, the reactor chamber was pumped down to a base pressure of less than 1.3 Pa (2 mTorr). A mixture of Ar (argon) and O₂ (oxygen) gas was flowed into the chamber, each at a rate of 100 SCCM. Treatment was carried out using a plasma enhanced CVD method by coupling RF power into the reactor at a frequency of 13.56 MHz and an applied power of 6000 watts. Treatment time was controlled by moving the microstructured film through the reaction zone. Following the treatment, the RF power and the gas supply were stopped and the chamber was returned to atmospheric pressure. Additional information regarding materials, processes for applying cylindrical RIE, and further details around the reactor used can be found in U.S. Pat. No. 8,460,568 B2.

Method for Back-Filling Channels of the Microstructured Film

The channels were back-filled with Resin A used in PE1 by pipetting the resin between the microstructured film surface and a piece of unprimed, 3 mil-thick PET film placed on top, using a hand roller to apply pressure to the top PET film, and then UV curing with a Heraeus (Hanau, Germany) belt conveyer UV processor (Model# DRS(6)) with an ‘H’ bulb at 500 Watt power. Specifically, the samples were sent through the UV curing station three times at a conveyer speed of 50 ft/min. Next, the top PET film was stripped off the microstructured film by hand.

Method for Measuring the Luminance Profile from a Diffuse Light Source

A sample of film was placed on a Lambertian light source. When the light transmissive regions are tapered, the film is positioned such that the widest portion of the tapered regions are closer to the light source. An Eldim L80 conoscope (Eldim S. A., HEROUVILLE SAINT CLAIR, France) was used to detect light output in a hemispheric fashion at all polar and azimuthal angles simultaneously. After detection, a cross section of transmission (e.g. brightness) readings were taken in a direction orthogonal to the direction of the louvers (denoted as a 0° orientation angle), unless indicated otherwise. Relative transmission (i.e. brightness of visible light) is defined as the percentage of on-axis luminance, at a certain viewing angle, between a reading with film and a reading without the film.

The Lambertian light source consisted of diffuse transmission from a light box having the baseline luminance profile depicted in FIG. 6. The light box was a six-sided hollow cube measuring approximately 12.5 cm×12.5 cm×11.5 cm (L×W×H) made from diffuse polytetrafluoroethylene (PTFE) plates of ^(˜)6 mm thickness. One face of the box was chosen as the sample surface. The hollow light box had a diffuse reflectance of ^(˜)0.83 measured at the sample surface (e.g. ^(˜)83%, averaged over the 400-700 nm wavelength range). During testing, the box was illuminated from within through a ^(˜)1 cm circular hole in the bottom of the box (opposite the sample surface, with the light directed toward the sample surface from inside). The illumination was provided using a stabilized broadband incandescent light source attached to a fiber-optic bundle used to direct the light (Fostec DCR-II with a 1 cm diameter fiber bundle extension from Schott-Fostec LLC, Marlborough Mass. and Auburn, N.Y.).

Method for Measuring the Transmission for Ultraviolet and Near Infrared Light

The transmission of ultraviolet (320-400 nm) and near infrared light (700-1400 nm) light was measured with a Lambda 1050 spectrophotometer (Perkin Elmer, Waltham, Mass.) with a variable angle transmittance sample holder (Catalog #PELA9042). Values reported in the Examples are arithmetic averages of the transmission from 320-400 nm (ultraviolet) or 700-1400 nm (near infrared) as specified and at either a +30° or +60° incidence angle as specified, measured at a single location on each sample.

Method for Cross-Sectional Scanning Electron Microscopy (SEM)

Cross-sections were prepared via freeze fracturing using liquid nitrogen. SEM images were acquired with a Hitachi SU-8230 (Hitachi, Ltd., Tokyo, Japan) instrument.

Comparative Example 1-2 (CE1-CE-2) are Commercially Available Light Control Films Comparative Example 3 (CE3)

Two sections (each 3″×3″) of the film from CE1 were overlaid and laminated together with an optically clear adhesive (8171, 3M Company, St. Paul, Minn.). One sheet was oriented perpendicular to the other. That is, the original directions of the channels were offset by 90° between the top sheet and bottom sheet.

Preparative Example 2 (PE2): Preparation of Coating Solutions

PDAC was diluted from 20 wt % to a concentration of 0.32 wt % with deionized (DI) water. PAA was diluted from 25 wt % to a concentration of 0.1 wt %, and the pH was adjusted to 4.0 with 1M NaOH. CAB-O-JET® 200 (COJ200), CAB-O-JET® 250C (COJ250C), CAB-O-JET® 260M (COJ260M), and CAB-O-JET® 352K (COJ352K) were each diluted to a concentration of 0.10 wt % with DI water. NaCl was added to both the PDAC solution and pigment suspensions to a concentration of 0.05 M. 1M NaOH was added to the COJ352K suspension to a pH of 9. pH values were measured with a VWR (West Chester, Pa.) pH electrode (Catalog #89231-582), which was calibrated with standard buffer solutions.

Preparative Example 3 (PE3): Preparation of Cationic Pigment

Polyethylenimine (PEI)-modified CAB-O-JET® 352K (COJ352K) carbon black nanopigment, abbreviated as PEI-COJ352K, was prepared as follows. PEI (MW25K) was diluted to make a 10 wt % solution. A mass of 3.2 grams of the 10 wt % PEI solution was diluted with DI water up to a mass of 794.7 grams. Next, 5.3 grams of as-received COJ352K at 15.03% solids was added dropwise to the 794.7 gram PEI solution with vigorous magnetic stirring resulting in a final concentrations of 0.1 wt % COJ352K and 0.04 wt % PEI. Size and zeta potential of the polyethylenimine (PEI)-modified CAB-O-JET® 352K (COJ352K) were measured using a Brookhaven Instruments Corp. (Holtsville, N.Y.) ZetaPALS instrument with an aliquot of the PEI-COJ352K sample above diluted by 100× with 1 mM KCl. Particle size was described by d₁₀=77.5 nm, d₅₀=148.4 nm, and d₉₀=284.0 nm. Zeta potential was measured to be +37.9±0.9 mV.

Example 1 (EX1): Carbon Black Nano-Pigment, 130 nm Diameter, not Back-Filled

A sheet of microstructured film as made in PE1 was cut to a size of 9″×10″ and corona treated by hand using a BD-20AC Laboratory Corona Treater (Electro-Technic Products, Chicago, Ill.) to prevent the aqueous coating solutions from beading up and dewetting. PDAC and CAB-O-JET® ® 200 coating solutions were made as described in PE2. The corona-treated film was coated with (PDAC/COJ200)₁₀ using the “Method for Making Spray Layer-by-Layer Self-Assembled Coatings on Microstructured Film”. This coated film was subjected to reactive ion etching (RIE) at a power of 6000 W for a duration of 210 s. An equivalent coating deposited onto a glass plate had a thickness of 166 nm as measured with a Dektak XT stylus profilometer (Bruker Nano, Inc., Tucson, Ariz.) after scoring the coating with a razor blade. Based on the thickness of the equivalent coating deposited on glass, the aspect ratio of the absorptive regions (e.g. louvers) was approximately 525:1.

Example 2 (EX2): Carbon Black Nano-Pigment, 130 nm Diameter, Back-Filled

A sheet of microstructured film as made in PE1 was cut to a size of 9″×10″ and corona treated by hand using a BD-20AC Laboratory Corona Treater (Electro-Technic Products, Chicago, Ill.) to prevent the aqueous coating solutions from beading up and dewetting. PDAC and CAB-O-JET® 200 coating solutions were made as described in PE2. The corona-treated film was coated with (PDAC/COJ200)₂₀ using the “Method for Making Spray Layer-by-Layer Self-Assembled Coatings on Microstructured Film”. This coated film was subjected to reactive ion etching (RIE) at a power of 6000 W for a duration of 210 s. Next, the channels were back-filled using the “Method for Back-Filling Channels of the Microstructured Film” described above. An equivalent coating deposited onto a glass plate had a thickness of 326 nm as measured with a Dektak XT stylus profilometer after scoring the coating with a razor blade.

Example 3 (EX3): Carbon Black Nano-Pigment, 70-80 nm Diameter, not Back-Filled

A sheet of microstructured film as made in PE1 was cut to a size of 9″×10″ and corona treated by hand using a BD-20AC Laboratory Corona Treater (Electro-Technic Products, Chicago, Ill.) to prevent the aqueous coating solutions from beading up and dewetting. PDAC and CAB-O-JET® 352K coating solutions were made as described in PE2. The corona-treated film was coated with (PDAC/COJ352K)₂₀ using the “Method for Making Spray Layer-by-Layer Self-Assembled Coatings on Microstructured Film”. The coated film was then subjected to reactive ion etching (RIE) at a power of 6000 W for a duration of 200 s. An equivalent coating deposited onto a glass plate had a thickness of 273 nm as measured by a Dektak XT stylus profilometer after scoring the coating with a razor blade.

Example 4-6 (EX4-6): Carbon Black Nano-Pigment, 70-80 nm Diameter, Back-Filled

Three sheets of microstructured film as made in PE1 were each cut to a size of 9″×10″ and corona treated by hand using a BD-20AC Laboratory Corona Treater (Electro-Technic Products, Chicago, Ill.) to prevent the aqueous coating solutions from beading up and dewetting. PDAC and CAB-O-JET® 352K coating solutions were made as described in PE2. Separate 9″×10″ pieces of the corona-treated films were coated with (PDAC/COJ352K)₂₀ (EX4), (PDAC/COJ352K)₄₀ (EX5), and (PDAC/COJ352K)₆₀ (EX6) using the “Method for Making Spray Layer-by-Layer Self-Assembled Coatings on Microstructured Film”. The coated films were subjected to reactive ion etching (RIE) at a power of 6000 W for durations of 200 s (EX4) and 500 s (EX5 & EX6). Cross-sectional SEM images were taken of EX4, before and after RIE, but prior to back-filling. It was evident from the SEM images that the coating deposited on the film was of a uniform thickness and the thickness corresponded with the equivalent coating deposited onto glass, described below. Next, the channels were back-filled using the “Method for Back-Filling Channels of the Microstructured Film” described above. The luminance profile from a diffuse light source was measured using the “Method for Measuring the Luminance Profile from a Diffuse Light Source” above (data in FIG. 6 and Tables 5A and 5B). Equivalent coatings deposited onto glass plates had thicknesses of 273 nm (EX4), 536 nm (EX5), and 796 nm (EX6) as measured with a Dektak XT stylus profilometer after scoring the coatings with a razor blade. Based on the thickness of the equivalent coatings deposited on glass, the aspect ratios of the absorptive regions (e.g. louvers) ranged from approximately 109:1 (for EX6) to 319:1 (for EX4).

TABLE 5A Relative brightness (RB) for EX2, EX4-EX6 and CE1-CE2. Avg. % % RB % RB % RB RB of +30° 0° at +30° at −30° and −30° # viewing viewing viewing viewing Ex. bilayers angle angle angle angles EX2 20 86.6 17.9 21.8 19.9 EX4 20 91.0 21.6 19.4 20.5 EX5 40 91.9 21.9 19.0 20.4 EX6 60 91.0 17.8 14.8 16.3 CE1 N/A 68.1 23.1 12.8 17.9 CE2 N/A 64.3 13.6 4.8 9.2

TABLE 5B Relative brightness (RB) for EX2, EX4-EX6 and CE1-CE2. Average % RB for Average Average viewing % RB % RB for % RB for angles from 0° viewing viewing +35° to +80° # viewing angles from angles from and Ex. bilayers angle +35° to +80° −35° to −80° −35° to −80° EX2 20 86.6 4.49 5.05 4.77 EX4 20 91.0 5.12 4.82 4.97 EX5 40 91.9 4.54 4.25 4.40 EX6 60 91.0 3.14 3.01 3.08 CE1 N/A 68.1 3.47 3.43 3.43 CE2 N/A 64.3 1.56 1.06 1.31

TABLE 5C Transmission of Ultraviolet and Near Infrared Light for EX6 UVA % T NIR % T Ex. 0° 30° 60° 0° 30° 60° CE1 29.3 4.8 0.0 62.8 9.9 0.0 EX6 56.8 3.6 0.04 74.9 4.3 0.3

Example 7 (EX7): Overlaid, Crossed Films

Two sections (each 3″×3″) of the light control film prepared according to EX4 were overlaid, with the structured sides facing each other, with one sheet being oriented perpendicular to the other. That is, the original direction of the channels was offset by 90° between the top sheet and bottom sheet. Resin A was dispensed between the two sheets and the two sheets were laminated together with a hand roller. The sample was cured as described in the “Method for Back-Filling Channels of the Microstructured Film,” and was measured using the “Method for Measuring the Luminance Profile from a Diffuse Light Source”. Data are in Table 6A and 6D.

Example 8 (EX8): Overlaid, Aligned Films

Two sections (each 3″×3″) of the light control film prepared according to EX4 were overlaid, with the structured sides facing each other, with one sheet being oriented parallel to the other. That is, the original direction of the channels was aligned between the top sheet and bottom sheet. Resin A was dispensed between the two sheets and the two sheets were laminated together with a hand roller. The sample was cured as described in the “Method for Back-Filling Channels of the Microstructured Film” and was measured using the “Method for Measuring the Luminance Profile from a Diffuse Light Source”. Data are in Tables 6A-6D.

TABLE 6A Relative brightness measured for EX7-EX8 and CE3. Avg. % RB % RB % RB % RB of +30° 0° at +30° at −30° and −30° viewing viewing viewing viewing Ex. angle angle angle angles EX7 88.5 19.6 22.9 21.3 EX8 90.6 5.13 7.69 6.41 CE3 55.9 6.93 11.0 8.97

TABLE 6B Relative brightness measured for EX7-EX8 and CE3. Average % RB for Average Average viewing % RB % RB for % RB for angles from 0° viewing viewing +35° to +80° viewing angles from angles from and Ex. angle +35° to +80° −35° to −80° −35° to −80° EX7 88.5 4.48 4.97 4.73 EX8 90.6 1.01 1.14 1.08 CE3 55.9 0.68 0.93 0.81

TABLE 6C Relative brightness measured for EX7-EX8 and CE3 at a 90° orientation angle. Avg. % % RB % RB % RB RB of +30° 0° at +30° at −30° and −30° viewing viewing viewing viewing Ex. angle angle angle angles EX7 88.5 19.1 19.1 19.1 EX8 90.6 90.4 88.9 89.6 CE3 55.9 6.66 12.8 9.73

TABLE 6D Relative brightness measured for EX7-EX8 and CE3 at a 90° orientation angle. Average % RB for Average Average viewing % RB % RB for % RB for angles from 0° viewing viewing +35° to +80° viewing angles from angles from and Ex. angle +35° to +80° −35° to −80° −35° to −80° EX7 88.5 4.41 4.59 4.50 EX8 90.6 80.6 78.5 79.5 CE3 55.9 0.67 1.19 0.93

Example 9A (EX9A): Cyan Nano-Pigment Coating, not Back Filled

A microstructured sheet of film as made in PE1 was cut to a size of 9″×10″ and corona treated by hand using a BD-20AC Laboratory Corona Treater (Electro-Technic Products, Chicago, Ill.) to prevent the aqueous coating solutions from beading up and dewetting. PDAC and CAB-O-JET® 250C coating solutions were made as described in PE2. The corona-treated film was coated with (PDAC/COJ250C)₂₀ using the “Method for Making Spray Layer-by-Layer Self-Assembled Coatings on Microstructured Film”. This coated film was subjected to reactive ion etching (RIE) at a power of 6000 W for a duration of 150 s. Relative brightness was measured using the “Method for Measuring the Luminance Profile from a Diffuse Light Source” (data in Table 7). An equivalent coating deposited onto a glass plate had a thickness of 340 nm as measured by a Dektak XT stylus profilometer (Bruker Nano, Inc., Tucson, Ariz.) after scoring the coating with a razor blade.

Example 9B (EX9B): Cyan Nano-Pigment Coating, Back-Filled

A microstructured sheet of film was prepared as described in 9A except that the channels were back-filled using the “Method for Back-Filling Channels of the Microstructured Film” described above. Relative brightness was measured using the “Method for Measuring the Luminance Profile from a Diffuse Light Source” (data in Table 7). An equivalent coating deposited onto a glass plate had a thickness of 340 nm as measured by a Dektak XT stylus profilometer (Bruker Nano, Inc., Tucson, Ariz.) after scoring the coating with a razor blade.

Example 10A (EX10A): Magenta Nano-Pigment Coating, not Back-Filled

A microstructured sheet of film as made in PE1 was cut to a size of 9″×10″ and corona treated by hand using a BD-20AC Laboratory Corona Treater (Electro-Technic Products, Chicago, Ill.) to prevent the aqueous coating solutions from beading up and dewetting. PDAC and CAB-O-JET® 260M coating solutions were made as described in PE2. The corona-treated film was coated with (PDAC/COJ260M)₂₀ using the “Method for Making Spray Layer-by-Layer Self-Assembled Coatings on Microstructured Film”. This coated film was subjected to reactive ion etching (RIE) at a power of 6000 W for a duration of 150 s. Relative brightness was measured using the “Method for Measuring the Luminance Profile from a Diffuse Light Source” (data in Table 7). An equivalent coating deposited onto a glass plate had a thickness of 313 nm as measured by a Dektak XT stylus profilometer (Bruker Nano, Inc., Tucson, Ariz.) after scoring the coating with a razor blade.

Example 10B (EX10B): Magenta Nano-Pigment Coating, Back-Filled

A microstructured sheet of film was prepared as described in 10A except that the channels were back-filled using the “Method for Back-Filling Channels of the Microstructured Film” described above. Relative brightness was measured using the “Method for Measuring the Luminance Profile from a Diffuse Light Source” (data in Table 7). An equivalent coating deposited onto a glass plate had a thickness of 313 nm as measured by a Dektak XT stylus profilometer (Bruker Nano, Inc., Tucson, Ariz.) after scoring the coating with a razor blade.

TABLE 7A Relative brightness for EX9-EX10 Avg. % RB of % RB % RB % RB +30° and RIE Resin 0° at +30° at −30° −30° # Time Back- viewing viewing viewing viewing Example bilayers (sec) Filled? angle angle angle angles EX9A 20 150 No 85.7 26.3 24.0 25.1 EX9B 20 150 Yes 89.4 47.0 40.1 43.5 EX10A 20 150 No 95.8 43.7 44.5 44.1 EX10B 20 150 Yes 95.0 63.3 64.7 64.1

TABLE 7B Relative brightness for EX9-EX10 Average % RB for Average Average viewing % RB % RB for % RB for angles from 0° viewing viewing +35° to +80° viewing angles from angles from and Ex. angle +35° to +80° −35° to −80° −35° to −80° EX9A  85.7 10.8 10.0 10.4 EX9B  89.4 23.8 23.4 23.6 EX10A 95.8 30.4 31.1 30.8 EX10B 95.0 44.1 45.3 44.7

TABLE 7C Transmission of Ultraviolet and Near Infrared Light for EX9A-EX10B UVA % T NIR % T Ex. 0° 30° 60° 0° 30° 60° EX9A 34.9 0.5 0.0 79.1 22.6 11.9 EX9B 49.4 6.6 3.4 75.2 63.2 62.0 EX10A 55.2 5.1 0.6 76.7 27.5 15.3 EX10B 52.4 33.1 24.5 75.3 71.3 76.2

Example 11 (EX 11): Cationic Pigment, Anionic Polyelectrolyte

A glass microscope slide (Fisher Scientific, Waltham, Mass.), 1″×3″ in size, was rinsed with DI water and isopropanol. The slide was mounted on a StratoSequence VI (nanoStrata, Inc., Tallahassee, Fla.) automated layer-by-layer dip coater. The slide was dipped in the PEI-COJ352K solution described in PE3 for 1 min. Next the slide was dipped in three consecutive DI water rinse baths for 30 sec each. Next, the slide was dipped in a PAA solution (0.1 wt %, adjusted to pH 4 with HCl) for 1 min. Next, the slide was dipped in three consecutive DI water rinse baths for 30 sec each. The slide was rotated at 150 rpm in each bath. This cycle was repeated for a total of 10 times to deposit (PEI-COJ352K/PAA)₁₀. The coating had a thickness of 4 μm as measured with a Dektak XT stylus profilometer (Bruker Nano, Inc., Tucson, Ariz.) after scoring the coating with a razor blade. The microstructured film of PE1 could be layer-by-layer coated with this composition and subjected to RIE as previously described.

Example 12 (EX 12): Cationic Pigment, Anionic Pigment

A glass microscope slide (Fisher Scientific, Waltham, Mass.), 1″×3″ in size, was rinsed with DI water and isopropanol. The slide was mounted on a StratoSequence VI (nanoStrata, Inc., Tallahassee, Fla.) automated layer-by-layer dip coater. The slide was dipped in the PEI-COJ352K solution (as described in PE3) for 1 min. Next the slide was dipped in three consecutive DI water rinse baths for 30 sec each. Next, the slide was dipped in a COJ352K solution (as described in PE2) for 1 min. Next, the slide was dipped in three consecutive DI water rinse baths for 30 sec each. The slide was rotated at 150 rpm in each bath. This cycle was repeated for a total of 10 times to deposit (PEI-COJ352K/COJ352K)₁₀. The coating had a thickness of 240 nm as measured with a Dektak XT stylus profilometer (Bruker Nano, Inc., Tucson, Ariz.) after scoring the coating with a razor blade. The microstructured film of PE1 could be layer-by-layer coated with this composition and subjected to RIE as previously described.

Example 13 (EX 13)

A light control film was prepared as described in EX. 1. During the method of back-filling the channels of the microstructured film, the top PET film was replaced with a color shifting film, as described by Example 1 of WO 2010/1090924. After UV curing the back-filled channels, this color shifting film was not stripped off, but instead retained as a cover film.

TABLE 8A Relative brightness for EX13 Average Average % RB % RB % RB % RB for % RB for 0° at +30° at −30° viewing viewing viewing viewing viewing angles from angles from Ex. angle angle angle +35° to +80° −35° to −80° EX13 120.6 20.7 21.5 3.7 4.0

The highly reflective color shifting film caused light recycling in the gain cube, resulting in the on-axis relative brightness being greater than 100%.

TABLE 8B Transmission of Ultraviolet and Near Infrared Light for EX13 UVA % T NIR % T Example 0° 30° 60° 0° 30° 60° EX 13 9.9 1.0 0.1 26.0 10.6 5.8

Surface Area of Absorptive Regions

The light input surface of CE2 was viewed with an optical microscope at 200× magnification. The maximum width of multiple absorptive regions (i.e., W_(A) in FIG. 1a ) and pitches (i.e., P_(A) in FIG. 1a ) were measured by analyzing the optical microscope images with ImageJ software (available from the National Institute of Health at the website http://imagej.nih.gov/ij). The average width of five absorptive regions was measured to be 14.7 microns. The average pitch was measured to be 64.9 microns. Thus, the ratio W_(A)/P_(A) equals 0.227, or 22.7% of the surface area.

The light input surface of EX6 was viewed with an optical microscope at 200× magnification. The maximum width of multiple absorptive regions (i.e., W_(A) in FIG. 1a ) and pitches (i.e., P_(A) in FIG. 1a ) were measured by analyzing the optical microscope images with ImageJ software (available from the National Institute of Health at the website http://imagej.nih.gov/ij). The average width of five absorptive regions was measured to be 1.0 microns. The average pitch was measured to be 31.2 microns. When the wall angle is zero, the ratio W_(A)/P_(A) equals 0.032, or 3.2% of the surface area. For the wall angle of 1.5 degrees, the surface area is 10.8%. 

1. A light control film, comprising: a light input surface and a light output surface opposite the light input surface; alternating transmissive regions and absorptive regions disposed between the light input surface and the light output surface, wherein the absorptive regions have an aspect ratio of at least 30 and the alternating transmissive region and absorptive regions have a transmission as measured with a spectrophotometer at a viewing angle of 0 degrees of i) at least 35% for a wavelength of the range 320-400 nm (UV), or ii) at least 65% for a wavelength of the range 700-1400 nm (NIR), or a combination thereof.
 2. The light control film of claim 1 wherein the absorptive regions have a width parallel to light input surface and a height orthogonal to the light input surface and the height is greater than the width.
 3. The light control film of claim 1 wherein the alternating transmissive regions and absorptive regions have a relative transmission of visible light at a viewing angle of +30 degrees or −30 degrees of less than 50%.
 4. The light control film of claim 1 wherein the alternating transmissive regions and absorptive regions have an average relative transmission of visible light for viewing angles ranging from +35 to +80 degrees or an average relative transmission for visible light for viewing angles ranging from −35 to −80 degrees of less than 10%.
 5. The light control film of claim 1 wherein the transmissive regions have a wall angle less than 5 degrees.
 6. The light control film of claim 1 wherein the transmissive regions and absorptive regions have a height ranging from 50 to 200 microns.
 7. The light control film of claim 1 wherein the absorptive region has an average width no greater than 5 microns.
 8. (canceled)
 9. The light control film of claim 1 wherein the absorptive regions have an average pitch of 10 to 200 microns. 10-13. (canceled)
 14. The light control film of claim 1 wherein the absorptive regions comprise polyelectrolytes.
 15. (canceled)
 16. The light control film of claim 1 wherein the alternating transmissive regions and absorption region are disposed on a base layer or the light control film further comprises a cover film and the base layer or cover film is a multilayer film selected from a color shifting film, a UV reflective film, a UV-blue reflective film, or a near infrared reflective film. 17-24. (canceled)
 25. A light control film comprising a first light control film according to claim 1 disposed upon a second light control film.
 26. The light control film of claim 25 wherein the second light control film is according to claim 1 and the first and second light control films are positioned such that the absorptive regions range from being parallel to orthogonal with each other at a viewing angle of 0 degrees or positioned such that the absorptive regions are coincident with each other at a viewing angle of 0 degrees. 27-33. (canceled)
 34. A light detection system, including: a light source configured to emit light having a first spectral profile along a first direction and a second spectral profile along a different second direction; a detector sensitive to wavelengths in a detection wavelength range; a light control film according to claim 1 disposed on the light source or detector for receiving and transmitting light emitted by the light source.
 35. The light detection system of claim 34 wherein the light source comprises a light emitting diode (LED), a laser light source, a halogen light source, a metal halide light source, a tungsten light source, a mercury vapor light source, a short arc xenon light source, or the sun.
 36. The light detection system of claim 34 wherein the detector comprises a photovoltaic device, a solar battery, a solar cell, a camera.
 37. The light detection system of claim 34 wherein the light control film is disposed on to the light source and the detector is remote.
 38. The light detection system of claim 34 wherein the light control film is disposed on to the detector and the light source is remote.
 39. The light detection system of claim 34 wherein the light detection system is a vehicle sensor.
 40. The light detection system of claim 34 wherein the light control film is disposed on a retroreflective sheet.
 41. The light detection system of claim 40 wherein retroreflective sheet comprises at least one of microsphere beads and corner cubes. 